金属/高分子ハイブリッド構造を作るための代替添加剤製造に基づく接合法【JST・京大機械翻訳】

An alternative additive manufacturing-based joining method to make Metal/Polymer hybrid structures

著者 (5件)： Ozlati A. (Department of Materials Science and Engineering, Sharif University of Technology, 11365-9466, Azadi Ave., Tehran, Iran) ,  Movahedi M. (Department of Materials Science and Engineering, Sharif University of Technology, 11365-9466, Azadi Ave., Tehran, Iran) ,  Tamizi M. (Department of Materials Science and Engineering, Sharif University of Technology, 11365-9466, Azadi Ave., Tehran, Iran) ,  Tartifzadeh Z. (Department of Materials Science and Engineering, Sharif University of Technology, 11365-9466, Azadi Ave., Tehran, Iran) ,  Alipour S. (Department of Materials Science and Engineering, Sharif University of Technology, 11365-9466, Azadi Ave., Tehran, Iran)
資料名： Journal of Manufacturing Processes  (Journal of Manufacturing Processes)
巻： 45  ページ： 217-226  発行年： 2019年 
JST資料番号： W3312A  ISSN： 1526-6125  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ポリプロピレンフィラメントを用いた溶融析出モデリングを用いて,高分子基板と添加部分の間の結合および添加部分とアルミニウムベースシートの間の機械的ロックの形で,ポリプロピレンとプレパンチAl-Mg合金シートの間の重ね継手を作った。継手の機械的性質に及ぼす接合界面面積(孔径5~13mm)および基板の予熱(室温,50および90°C)の影響を調べた。引張せん断および交差引張試験におけるピーク荷重は,接合界面面積(それぞれ280Nおよび160Nまで)の増加とともに増加した。引張-せん断試験における高い継手強度を,交差引張試験と比較して,試験における破壊位置の観点から検討した。基板の予熱は,高分子シートと添加部分の間の結合の改善と印刷層間の接着力の増加を介して継手強度を増加させた。Copyright 2019 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 剪断試験 ,  重ね継手 ,  アルミニウム ,  剪断 ,  合金 ,  付着力 ,  予熱 ,  引張 ,  モデリング ,  機械的性質 ,  フィラメント ,  *接合 ,  引張試験
準シソーラス用語： 継手強度 ,  接合界面 , 【Automatic Indexing@JST】

著者キーワード (6件)： 添加剤製造 ,  金属/高分子ハイブリッド構造 ,  溶融堆積モデリング ,  ポリプロピレン ,  アルミニウム ,  機械的性質

分類 (2件)： 機械加工,仕上げ一般  (YH04111G) ,  機械的性質  (WB02030U)