近αチタン合金のミクロ組織と機械的性質に及ぼすホウ素添加法の影響【JST・京大機械翻訳】

Effect of Boron Addition Methods on Microstructure and Mechanical Properties of a Near-α Titanium Alloy

著者 (6件)： Liu Yingying (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Chai Lihua (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Ma Xiaozhao (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Cui Yapeng (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Chen Ziyong (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China) ,  Xiang Zhilei (College of Materials Science and Engineering, Beijing University of Technology, Beijing, China)
資料名： Springer Proceedings in Physics  (Springer Proceedings in Physics)
巻： 217  ページ： 51-64  発行年： 2019年 
JST資料番号： W5066A  ISSN： 0930-8989  資料種別： 会議録 (C)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本研究では,近αチタン合金のミクロ組織と機械的性質に及ぼすホウ素添加法の影響を調べた。マトリックスとしてTi-6.5Al-2.5Sn-9Zr-0.5Mo-1W-1Nb-0.25Siを用い,0.3wt%TiB_2と0.1wt%Bを添加した。結果は,微量ホウ素の添加が,前のβ粒界にTiBホイスカを形成し,ベース合金における微細構造の著しい微細化をもたらすことを示した。また,ベース合金に及ぼす0.3wt%TiB_2および0.1wt%Bの微細化効果は類似していた。室温では,ホウ素含有合金の強度は一定の増加を示したが,伸びはわずかに低下した。引張歪試験片の微細構造に関する研究を通して,ホウ素含有合金の引張強さの増加はベース微細構造とホイスカ軸受の組合せであるが,延性低下は主にTiB相の亀裂に起因することを見出した。Copyright 2019 Springer Nature Singapore Pte Ltd. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *チタン合金 ,  精密化 ,  微細構造 ,  伸び ,  亀裂 ,  軸受 ,  *金属組織 ,  ホイスカ ,  機械的性質 ,  *ホウ素 ,  結晶粒界 ,  引張強さ ,  ホウ素含有合金 ,  延性
準シソーラス用語： 引張歪 , 【Automatic Indexing@JST】

著者キーワード (4件)： チタン合金 ,  TiBホイスカ ,  微細構造 ,  機械的性質

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： チタン合金 ,  ミクロ組織 ,  機械的性質 ,  ホウ素