ボトムアップ加工多結晶ダイヤモンドフォトニック結晶スラブを用いたシリコン空格子点中心発光の増強抽出【JST・京大機械翻訳】

Enhanced Extraction of Silicon-Vacancy Centers Light Emission Using Bottom-Up Engineered Polycrystalline Diamond Photonic Crystal Slabs

著者 (6件)： Ondic Lukas (Institute of Physics, Academy of Sciences of the Czech Republic, Czech Republic) ,  Varga Marian (Institute of Physics, Academy of Sciences of the Czech Republic, Czech Republic) ,  Hruska Karel (Institute of Physics, Academy of Sciences of the Czech Republic, Czech Republic) ,  Fait Jan (Institute of Physics, Academy of Sciences of the Czech Republic, Czech Republic) ,  Fait Jan (Faculty of Electrical Engineering, Czech Technical University in Prague, Czech Republic) ,  Kapusta Peter (J. Heyrovsky Institute of Physical Chemistry, Academy of Sciences of the Czech Republic, Czech Republic)
資料名： ACS Nano  (ACS Nano)
巻： 11  号： 3  ページ： 2972-2981  発行年： 2017年03月 
JST資料番号： W2326A  ISSN： 1936-0851  CODEN： ANCAC3  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： シリコン空格子点(SiV)中心はダイヤモンド中の光学的に活性な欠陥である。窒素空格子点(NV)中心と対照的に,SiV中心は室温でも狭く効率的なルミネセンススペクトル(約738nmを中心とする)を有し,量子フォトニクスとセンシング応用に利用できる。しかし,ダイヤモンドで発生する光の大部分は,全内部反射現象により材料中にトラップされる。この問題を克服するために,石英テンプレート上にボトムアップ成長を用いて高密度のSiV中心を有する多結晶ダイヤモンド薄層から二次元フォトニック結晶スラブを調製した。SiV中心の狭い発光と発光をほぼ垂直方向に抽出する漏れモード(容易に検出できる)の間のスペクトル重なりが蒸着時間を制御することにより得られることを示した。非波形試料と比較して,SiV中心光ルミネセンスの14倍以上の抽出増強が達成された。計算機シミュレーションは,抽出増強がSiV中心から放出された光とフォトニック結晶スラブとの間の効率的な光-物質相互作用に起因することを確認した。Copyright 2019 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 全反射 ,  *発光 ,  蒸着 ,  *フォトニック結晶 ,  石英 ,  *ケイ素 ,  薄膜 ,  発光スペクトル ,  *ダイヤモンド ,  計算機シミュレーション ,  *空格子点 ,  光ルミネセンス
準シソーラス用語： フォトニクス ,  *多結晶ダイヤモンド ,  *ボトムアップ , 【Automatic Indexing@JST】

著者キーワード (5件)： シリコン空格子点中心 ,  光ルミネセンス ,  フォトニック結晶スラブ ,  漏れモード ,  多結晶ダイヤモンド