ショットピーニングした4340M鋼の100,200,300%被覆率の疲労寿命の比較【JST・京大機械翻訳】

A Comparison of the Fatigue Life of Shot-Peened 4340M Steel with 100, 200, and 300% Coverage

著者 (8件)： AlSumait A. (Mechanical Engineering Department, Loyola Marymount University, Los Angeles, CA, USA) ,  Li Y. (Mane Laboratories, College of Science and Engineering, Loyola Marymount University, Los Angeles, CA, USA) ,  Weaser M. (Moog Incorporated, Torrance, CA, USA) ,  Niji K. (Moog Incorporated, Torrance, CA, USA) ,  Battel G. (Moog Incorporated, Torrance, CA, USA) ,  Toal R. (Electrical Engineering and Computer Science Department, Loyola Marymount University, Los Angeles, CA, USA) ,  Alvarez C. (Mechanical Engineering Department, Loyola Marymount University, Los Angeles, CA, USA) ,  Es-Said O. S. (Mechanical Engineering Department, Loyola Marymount University, Los Angeles, CA, USA)
資料名： Journal of Materials Engineering and Performance  (Journal of Materials Engineering and Performance)
巻： 28  号： 3  ページ： 1780-1789  発行年： 2019年 
JST資料番号： C0161B  ISSN： 1059-9495  CODEN： JMEPEG  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： ショットピーニングは,構造部品の疲労性能を改善するために広く使われてきた。本研究の目的は,ショットピーニングにより4340M鋼の疲れ寿命を増加させ,3つの異なるショットピーニング被覆率(100,200および300%)での性能を比較することである。結果は,4340M鋼の最適被覆率がこの実験で200%であることを示した。走査電子顕微鏡(SEM)を用いて微細構造特性を評価し,得られた亀裂の深さと長さを推定した。更なる検証を必要とする提案した革新的技術を適用して,SEMが3つの被覆の外観を区別することを可能にした。X線回折を用いて測定した残留応力は,200%被覆率が比較的高い残留圧縮応力を有することを示した。Copyright 2019 ASM International Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *鋼 ,  走査電子顕微鏡 ,  X線回折 ,  亀裂 ,  微細構造 ,  *被覆率 ,  *疲れ寿命 ,  *ショットピーニング ,  残留応力

著者キーワード (3件)： 4340M鋼 ,  疲労寿命 ,  ショットピーニング被覆率の割合

分類 (1件)： 熱的操作によらぬ硬化  (WC04080O)

タイトルに関連する用語 (3件)： ショットピーニング ,  被覆率 ,  疲労寿命