2D膜の外因性カチオン選択性【JST・京大機械翻訳】

Extrinsic Cation Selectivity of 2D Membranes

著者 (9件)： Walker Michael I. (Cavendish Laboratory, University of Cambridge, United Kingdom) ,  Ubych Krystian (Cavendish Laboratory, University of Cambridge, United Kingdom) ,  Saraswat Vivek (Department of Materials Science and Metallurgy, University of Cambridge, United Kingdom) ,  Chalklen Edward A. (Department of Engineering, University of Cambridge, United Kingdom) ,  Braeuninger-Weimer Philipp (Department of Engineering, University of Cambridge, United Kingdom) ,  Caneva Sabina (Department of Engineering, University of Cambridge, United Kingdom) ,  Weatherup Robert S. (Department of Engineering, University of Cambridge, United Kingdom) ,  Hofmann Stephan (Department of Engineering, University of Cambridge, United Kingdom) ,  Keyser Ulrich F. (Cavendish Laboratory, University of Cambridge, United Kingdom)
資料名： ACS Nano  (ACS Nano)
巻： 11  号： 2  ページ： 1340-1346  発行年： 2017年02月 
JST資料番号： W2326A  ISSN： 1936-0851  CODEN： ANCAC3  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： グラフェン及び六方晶窒化ホウ素(h-BN)の多孔質2D膜を横切る正及び負イオンの濃度駆動拡散の系統的研究から,それらのカチオン選択性を証明した。異なる塩濃度の貯留層を分離するグラフェンとh-BN単分子層の電流-電圧特性を用いて,選択性の尺度として反転ポテンシャルを計算した。塩濃度を交換することによりDebye遮蔽長を調整し,負の表面電荷がカチオン選択性をもたらすことを実証した。驚くべきことに,h-BNとグラフェン膜は類似の特性を示し,水性溶媒中での選択性の共通の起源を強く示唆した。初めて,カチオンフラックスは,オゾンを用いることにより増加し,グラフェン中に追加の細孔を形成し,一方,優れた選択性を維持することを実証した。浸透力変換を含む応用のために2D膜を使用するための拡張可能な方法を利用する機会を論じた。Copyright 2019 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： アニオン ,  電荷 ,  電流電圧特性 ,  *二次元 ,  細孔 ,  表面電荷 ,  浸透 ,  グラフェン ,  オゾン ,  単分子層 ,  多孔性 ,  *カチオン
準シソーラス用語： 貯留層 ,  塩濃度 ,  六方晶窒化ホウ素 , 【Automatic Indexing@JST】

著者キーワード (5件)： 多孔質2D材料 ,  グラフェン ,  六方晶系窒化ホウ素 ,  電荷選択 ,  欠陥

分類 (3件)： 炭素とその化合物  (YB02060D) ,  静電機器  (NB10020R) ,  原子・分子のクラスタ  (BH09030O)

タイトルに関連する用語 (3件)： 2D ,  カチオン ,  選択性