油-水分離のための超疎水性-超親油性PVDF-SiO_2ナノファイバー膜【JST・京大機械翻訳】

Electrospinning superhydrophobic-superoleophilic PVDF-SiO₂ nanofibers membrane for oil-water separation

著者 (6件)： Jiang Shan (School of Materials Science & Engineering, Changzhou University, Changzhou, China) ,  Meng Xiangfei (School of Materials Science & Engineering, Changzhou University, Changzhou, China) ,  Chen Binling (Changzhou Institute of Advanced Materials, Beijing University of Chemical Technology, Changzhou, China) ,  Wang Nannan (Changzhou Institute of Advanced Materials, Beijing University of Chemical Technology, Changzhou, China) ,  Wang Nannan (Inorganic Fullerene Center, School of Resources Environment and Materials, University of Guangxi, Nanning, Guangxi, P. R. China) ,  Chen Guangkai (Changzhou Institute of Advanced Materials, Beijing University of Chemical Technology, Changzhou, China)
資料名： Journal of Applied Polymer Science  (Journal of Applied Polymer Science)
巻： 137  号： 47  ページ： e49546  発行年： 2020年 
JST資料番号： C0467A  ISSN： 0021-8995  CODEN： JAPNAB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 油-水分離は,環境と人間が引き起こす油性廃水の損傷のために,研究興味を引きつけた。エレクトロスピニング繊維膜は高い油-水分離性能を有する。原料としてポリ(フッ化ビニリデン)(PVDF)-シリカブレンド溶液を用いたエレクトロスピニングにより,多段粗さを有するナノファイバ膜を調製した。結果は,SiO_2含有量が0から3wt%に増加したとき,ナノファイバ膜の水接触角(WCA)が138.5±1°Cから15.0±1.5°に促進されることを示した。ナノファイバ膜は重力駆動下で優れた分離効率(99±0.1%)を示し,高い分離フラックスは1857±101L・m-2・h-1であった。より重要なことに,得られたPVDF-SiO_2ナノファイバ膜は優れた多サイクル性能と安定な耐化学性を示し,油-水分離の実用化に大きな利点をもたらした。Copyright 2020 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  重力 ,  含油廃水 ,  表面粗さ ,  耐化学性 ,  分離効率 ,  *エレクトロスピニング ,  ナノ粒子
準シソーラス用語： 分離性能 ,  *超疎水性 ,  水接触角 ,  サイクル性能 ,  *一酸化ケイ素 ,  ナノファイバ膜 , 【Automatic Indexing@JST】

著者キーワード (6件)： 複合材料 ,  膜 ,  ナノ結晶 ,  ナノ粒子 ,  ナノワイヤ ,  表面と界面

分類 (1件)： その他の紡糸・製糸  (YM03050G)

タイトルに関連する用語 (6件)： 油 ,  水 ,  疎水性 ,  親油性 ,  PVDF ,  ナノファイバー膜