新しい高Q Mg_2LaNbO_6セラミックの焼結特性とマイクロ波誘電特性【JST・京大機械翻訳】

Sintering characteristics and microwave dielectric properties of new high-Q Mg₂LaNbO₆ ceramics

著者 (5件)： Xia Wang-Suo (School of Physical science and technology, China University of Mining and Technology, Xuzhou 221116, People’s Republic of China) ,  Zhang Shao-Bo (School of Physical science and technology, China University of Mining and Technology, Xuzhou 221116, People’s Republic of China) ,  Zhang Wen-Hu (School of Physical science and technology, China University of Mining and Technology, Xuzhou 221116, People’s Republic of China) ,  Wang Ying (School of Physical science and technology, China University of Mining and Technology, Xuzhou 221116, People’s Republic of China) ,  Shi Li-Wei (School of Physical science and technology, China University of Mining and Technology, Xuzhou 221116, People’s Republic of China)
資料名： Materials Research Express  (Materials Research Express)
巻： 6  号： 11  ページ： 116325 (6pp)  発行年： 2019年 
JST資料番号： W5570A  ISSN： 2053-1591  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高品質因子(Q×f)と近ゼロ周波数温度係数(τ_f)を有するMg_2LaNbO_6の新しいマイクロ波誘電セラミックを,従来の固相反応によって合成した。Mg_2LaNbO_6セラミックの焼結特性,結晶構造,およびマイクロ波誘電特性を特性評価し,研究した。結果として,Mg_2LaNbO_6セラミックは複雑な相組成を有し,LaNbO_4とMgOはそれぞれ主相と第二相であり,未知相(MgOに関連する)が検出された。Mg_2LaNbO_6セラミックの良く発達した微細構造を,設計した焼結温度域で得て,粒度とその分布も調査した。さらに,密度に関連する誘電率(ε_r)はほとんど変化しなかった。Q×f値は最初に増加し,次に減少した。それは粒径とその分布によって支配された。さらに,Mg_2LaNbO_6セラミックのτ_f値は比較的安定で,ゼロに近かった。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *マイクロ波 ,  *セラミック ,  粒径 ,  結晶構造 ,  キャラクタリゼーション ,  誘電率 ,  粒度 ,  固相反応 ,  相組成 ,  *焼結性 ,  微細構造 ,  酸化マグネシウム
準シソーラス用語： 焼結温度 ,  品質因子 ,  *マイクロ波誘電特性 , 【Automatic Indexing@JST】