反ペロブスカイト構造Li_2OHBrの室温合成【JST・京大機械翻訳】

Room temperature synthesis of anti-perovskite structured Li₂OHBr

著者 (4件)： Sugumar Manoj Krishna (Department of Material Design Innovation Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603, Japan) ,  Yamamoto Takayuki (Department of Material Design Innovation Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603, Japan) ,  Motoyama Munekazu (Department of Material Design Innovation Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603, Japan) ,  Iriyama Yasutoshi (Department of Material Design Innovation Engineering, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603, Japan)
資料名： Solid State Ionics  (Solid State Ionics)
巻： 349  ページ： Null  発行年： 2020年 
JST資料番号： B0096B  ISSN： 0167-2738  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： リチウムに富む反ペロブスカイト(LiRAP)構造Li+導体はソフトであり,潜在的に高いLi+導電性材料であることが報告されている。本論文では,LiOHおよびLiBr粉末のボールミル粉砕により,室温で部分的に水和したLiRAP,Li_2OHBrを製造するための新しい合成法について報告した。得られたLi_2OHBrは,254°Cで融点を有する立方相(a=4.046Å)として形成された。Li_2OHBrのリチウムイオン伝導率は,活性化エネルギー0.54eVで,25°Cで1.1×10-6Scm-1であった。得られたLi_2OHBrは60°C,50μA cm-2で100サイクルの安定なリチウムめっき/ストリッピング反応を繰り返した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 活性化エネルギー ,  固相反応 ,  粉体 ,  *リチウム ,  めっき ,  固体電解質 ,  水和 ,  融点 ,  臭化リチウム ,  導体材料 ,  導体 ,  *ペロブスカイト型構造 ,  イオン伝導率 ,  全固体電池
準シソーラス用語： ボールミル摩砕 , 【Automatic Indexing@JST】

著者キーワード (4件)： リチウムリッチ反ペロブスカイト ,  固体電解質 ,  全固体電池 ,  固相反応

分類 (3件)： 二次電池  (YB04030K) ,  塩  (CD01050V) ,  電気化学一般  (CB07010N)

タイトルに関連する用語 (2件)： ペロブスカイト構造 ,  室温