溶媒溶解を用いたナイロン6/セルロースナノ結晶複合膜の製造【JST・京大機械翻訳】

Production of Nylon-6/Cellulose Nanocrystal Composite Films Using Solvent Dissolution

著者 (4件)： Sucharitpong Thamonwan (Biotechnology of Biopolymers and Bioactive Compounds Special Research Unit, Department of Biotechnology, Faculty of Agro-Industry, Kasetsart University, Bangkok, Thailand) ,  Lam Nga Tien (Biotechnology of Biopolymers and Bioactive Compounds Special Research Unit, Department of Biotechnology, Faculty of Agro-Industry, Kasetsart University, Bangkok, Thailand) ,  Sukyai Prakit (Biotechnology of Biopolymers and Bioactive Compounds Special Research Unit, Department of Biotechnology, Faculty of Agro-Industry, Kasetsart University, Bangkok, Thailand) ,  Sukyai Prakit (Center for Advanced Studies for Agriculture and Food, Kasetsart University Institute for Advanced Studies, Kasetsart University, Bangkok, Thailand)
資料名： Sugar Tech  (Sugar Tech)
巻： 22  号： 2  ページ： 328-339  発行年： 2020年 
JST資料番号： W4975A  ISSN： 0972-1525  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： ナイロン-6(N6)複合材料を,溶媒溶解によりサトウキビバガスから抽出したセルロースナノ結晶(CNC)と組み込んだ。CNC含有量の影響を0,1,3,5および7wt%で評価した。原子間力顕微鏡画像は,得られたCNCの直径と長さがそれぞれ52.4±14.8と400.38±104.8nmであることを示した。Fourier変換赤外分析は,より高いCNC含有量の複合材料におけるセルロースの支配的ピーク強度の増加を示した。X線回折と機械分析により,1wt%のCNCを負荷したときの結晶度指数とYoung率の最適な改善を決定し,それぞれ64.37±0.12%と675.27MPaの値を得た。N6/CNC複合材料の最も高い不透明度値は,N6/CNC-7%に対して,8.592±0.062であった。さらに,CNCはN6複合材料の熱特性を低下させた。これらの結果は,CNCがN6高分子を強化する大きな可能性を有することを示唆した。Copyright Society for Sugar Research & Promotion 2019 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  Young率 ,  熱特性 ,  高分子 ,  結晶度 ,  Fourier変換 ,  複合材料 ,  *溶解 ,  赤外線 ,  原子間力顕微鏡 ,  *セルロース ,  *複合膜
準シソーラス用語： 不透明度 ,  サトウキビバガス ,  *セルロースナノ結晶 , 【Automatic Indexing@JST】

著者キーワード (4件)： ナイロン6 ,  サトウキビバガス ,  セルロースナノ結晶 ,  溶媒溶解

分類 (1件)： 充填剤,補強材  (YH05030J)

タイトルに関連する用語 (5件)： 溶媒 ,  溶解 ,  ナイロン6 ,  セルロースナノ結晶 ,  複合膜