360°C/18.6MPaにおける純水中のZr-Sn-Nb-Fe-Mo合金の腐食挙動:耐食性に及ぼす焼なまし温度の影響【JST・京大機械翻訳】

Corrosion behaviors of Zr-Sn-Nb-Fe-Mo alloys in pure water at 360 °C/18.6 MPa: Influence of annealing temperature on the anti-corrosion properties

著者 (4件)： Shi Huigang (State Key Laboratory of Metal Matrix Composites, School of Material Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Li Jiuxiao (School of Materials Engineering, Shanghai University of Engineering Science, Shanghai, 201620, PR China) ,  Mao Jianwei (State Key Laboratory of Metal Matrix Composites, School of Material Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Lu Weijie (State Key Laboratory of Metal Matrix Composites, School of Material Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China)
資料名： Corrosion Science  (Corrosion Science)
巻： 163  ページ： Null  発行年： 2020年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Zr-Sn-Nb-Fe-Mo合金を2つの異なる温度(480と550°C)で熱処理した。550°Cでアニールしたとき,より良好な耐食性が得られた。より低い酸化速度は,結晶粒界が酸素拡散の最も一般的な短絡経路であるので,酸化物粒界面積の減少に起因する。二つの機構が酸化物中の亀裂形成の原因である:正方晶から単斜晶への相転移と析出物の遅延酸化。亀裂は連続的に発生し,長い亀裂を形成するために連結し,酸化物膜の層間剥離と酸化物中の応力緩和をもたらす。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 単斜晶系 ,  *耐食性 ,  亀裂 ,  応力緩和 ,  結晶粒界 ,  析出物 ,  相転移 ,  酸化膜 ,  ジルコニウム合金 ,  酸化 ,  層間剥離 ,  酸化物 ,  正方晶系 ,  *合金
準シソーラス用語： 酸化速度 , 【Automatic Indexing@JST】

著者キーワード (5件)： ジルコニウム合金 ,  Raman分光法 ,  亀裂形成 ,  耐食性 ,  応力分布

分類 (2件)： 腐食  (WB03030B) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (9件)： 純水 ,  Zr ,  Sn ,  Nb ,  Fe ,  Mo合金 ,  腐食挙動 ,  耐食性 ,  焼なまし温度