多軸鍛造を用いた316Lステンレス鋼の微細組織変化と機械的性質【JST・京大機械翻訳】

Microstructural evolution and mechanical properties of 316L stainless steel using multiaxial forging

著者 (5件)： Rajput S.K. (Department of Mechanical Engineering, Bundelkhand Institute of Engineering and Technology, Jhansi, India) ,  Kumar Jitendra (Department of Mechanical Engineering, Bundelkhand Institute of Engineering and Technology, Jhansi, India) ,  Mehta Yashwant (Department of Metallurgical and Materials Engineering, National Institute of Technology, Srinagar, India) ,  Soota Tarun (Department of Mechanical Engineering, Bundelkhand Institute of Engineering and Technology, Jhansi, India) ,  Saxena K.K. (Department of Mechanical Engineering, GLA University, Mathura, India)
資料名： Advances in Materials and Processing Technologies  (Advances in Materials and Processing Technologies)
巻： 6  号： 3  ページ： 509-518  発行年： 2020年 
JST資料番号： W5756A  ISSN： 2374-068X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ABSTRACT:微細構造進展と機械的特性に及ぼす多軸鍛造の効果を調べるために,ステンレス鋼316Lの温間多軸鍛造(MAF)を行った。MAF316Lステンレス鋼は,体内インプラントのような幅広い応用に用いられるより高い比強度を示す。本研究では,ステンレス鋼316Lを,1.4,2.8および4.2の累積歪に対して600°Cで高温多軸鍛造し,それらの微細組織変化および機械的性質を調べた。微細構造の発達は光学顕微鏡を用いて見られ,パスによる粒径の連続的減少を観察した。材料の平均粒径は9パス後に37μmから8μmに減少した。材料の硬度は歪硬化とHall-Petch強化の組合せによって増加した。破壊型はSEMの助けで明確に見える。ディンプルのサイズはパスの増加とともに連続的に減少し,ピークと谷は材料中にいくつかの脆性の導入によって形成される。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 機械的性質 ,  高温 ,  微細構造 ,  *ステンレス鋼 ,  光学顕微鏡 ,  脆性 ,  粒径 ,  結晶粒微細化 ,  歪硬化 ,  硬度
準シソーラス用語： 比強度 ,  ディンプル ,  *SUS316L ,  *多軸鍛造 ,  微細構造進展 , 【Automatic Indexing@JST】

著者キーワード (5件)： 316Lステンレス鋼 ,  温間多軸鍛造 ,  結晶粒微細化 ,  微細構造進化 ,  フラクトグラフィ