中炭素高けい素鋼の黒鉛化挙動とその温度と粒径に対する依存性【JST・京大機械翻訳】

Graphitization behavior of medium-carbon high-silicon steel and its dependence on temperature and grain size

著者 (4件)： Kim Ye Jin (School of Materials Science and Engineering, Kyungpook National University, Daegu, 41566, Republic of Korea) ,  Bae Sang Woo (School of Materials Science and Engineering, Kyungpook National University, Daegu, 41566, Republic of Korea) ,  Lim Nam Suk (POSCO Technical Research Laboratories, POSCO, Pohang, 37859, Republic of Korea) ,  Park Sung Hyuk (School of Materials Science and Engineering, Kyungpook National University, Daegu, 41566, Republic of Korea)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 785  ページ： Null  発行年： 2020年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 中炭素,高ケイ素鋼(Fe-0.55C-2.3Si)の黒鉛化挙動を,黒鉛化速度と機械的性質に及ぼす熱処理温度と初期結晶粒サイズの影響に特に焦点を当てて研究した。熱処理の進行とともに,セメンタイト層の分解のためにパーライトは徐々に消失し,グラファイトは炭素原子の拡散と凝集のために形成される。これらの発生は材料の硬度を徐々に低下させる。より高い熱処理温度は黒鉛化挙動を促進し,その結果,黒鉛化の完了に要する時間の減少と平均グラファイトサイズの増加をもたらす。グラファイトは,これらの境界における高エネルギーと不規則な原子配列のために,結晶粒界で主に形成される。さらに,結晶粒界はグラファイト核形成サイトとして作用するので,より小さい粒径はより速い黒鉛化とより微細でより豊富なグラファイトの形成に対応する。完全な黒鉛化処理は材料の引張および圧縮強度の著しい低下と延性および低温鍛造性のかなりの改善を引き起こす。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  核形成 ,  凝集 ,  結晶粒界 ,  低温 ,  熱処理 ,  *炭素 ,  *黒鉛化 ,  セメンタイト ,  パーライト ,  グラファイト ,  *温度依存性 ,  引張 ,  圧縮強さ ,  *ケイ素鋼 ,  結晶粒径

著者キーワード (5件)： 高けい素鋼 ,  黒鉛化 ,  微細構造 ,  硬さ ,  機械的性質