CeCl_3溶液の電気変換による酸素空孔制御CeO_2の調製とその酸化機構【JST・京大機械翻訳】

Preparation of oxygen vacancy-controllable CeO₂ by electrotransformation of a CeCl₃ solution and its oxidation mechanism

著者 (6件)： Liu Jiang (School of Metallurgy, Northeastern University, Shenyang, 110819, China) ,  Liu Jiang (Key Laboratory of Ecological Metallurgy of Multi-metal Intergrown Ores of Ministry of Education, Shenyang, 110819, China) ,  Dou Zhihe (School of Metallurgy, Northeastern University, Shenyang, 110819, China) ,  Dou Zhihe (Key Laboratory of Ecological Metallurgy of Multi-metal Intergrown Ores of Ministry of Education, Shenyang, 110819, China) ,  Zhang Ting-an (School of Metallurgy, Northeastern University, Shenyang, 110819, China) ,  Zhang Ting-an (Key Laboratory of Ecological Metallurgy of Multi-metal Intergrown Ores of Ministry of Education, Shenyang, 110819, China)
資料名： Ceramics International  (Ceramics International)
巻： 46  号： 5  ページ： 5976-5982  発行年： 2020年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： CeO_2を,以前の研究においてCeCl_3溶液の電気変換によって首尾よく調製した。本研究では,Ce3+の酸化機構をサイクリックボルタンメトリーと電位-pH図により決定し,Ce3+が電気変換中に酸素により酸化され,溶液中の酸素含有量の重要な役割を確認した。したがって,CeO_2調製に及ぼす雰囲気(空気/アルゴン/酸素)の影響を,ガス型と流量を調整することによって研究した。XRDパターンは,CeO_2の立方晶蛍石構造と粒径を示した。ガス流量の増加とともに,粒径は減少したが,粒子サイズは増加した。この結果は,より小さい結晶粒がより多くの格子欠陥とより高い表面エネルギーを含むので,粒子が凝集するのを優先し,より大きな粒子を形成することを示した。XPSスペクトルは,CeO_2試料中にCe3+とCe4+の両方が存在することを証明した。Raman散乱は,より多くの酸素空格子点がアルゴン雰囲気と高いガス流で生成できることを明らかにした。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 粒度 ,  格子欠陥 ,  *酸素 ,  スペクトル ,  Raman散乱 ,  サイクリックボルタンメトリー ,  気体流 ,  *電気変換 ,  電位 ,  X線回折分析 ,  流量 ,  立方晶系 ,  X線回折 ,  結晶粒 ,  表面エネルギー ,  粒径

著者キーワード (4件)： 電気変換 ,  大気 ,  CeO_2微細構造 ,  酸素空孔

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  無機化合物のルミネセンス  (BM08093J)

タイトルに関連する用語 (5件)： 溶液 ,  電気変換 ,  酸素空孔 ,  調製 ,  酸化機構