J-GLOBAL ID：202002223516525631   整理番号：20A2275801

Ni-Ti合金の耐食性に及ぼすPACVDおよびRMS法により堆積した炭素層の影響【JST・京大機械翻訳】

Effect of Carbon Layers Deposited by PACVD and RMS Methods on Corrosion Resistance of Ni-Ti Alloy

著者 (4件)： Kaczmarek Marcin (Department of Biomaterials and Medical Devices Engineering, Faculty of Biomedical Engineering, Silesian University of Technology, Zabrze, Poland) ,  Kurtyka Przemyslaw (Department of Biomaterials and Medical Devices Engineering, Faculty of Biomedical Engineering, Silesian University of Technology, Zabrze, Poland) ,  Paszenda Zbigniew (Department of Biomaterials and Medical Devices Engineering, Faculty of Biomedical Engineering, Silesian University of Technology, Zabrze, Poland) ,  Basiaga Marcin (Department of Biomaterials and Medical Devices Engineering, Faculty of Biomedical Engineering, Silesian University of Technology, Zabrze, Poland)
資料名： Advances in Intelligent Systems and Computing  (Advances in Intelligent Systems and Computing)
巻： 1223  ページ： 279-287  発行年： 2020年 
JST資料番号： W5075A  ISSN： 2194-5357  資料種別： 会議録 (C)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本論文は,改良Ni-Ti合金の耐食性の結果を示した。提案した表面改質は,次の処理,粉砕,機械的研磨,および炭素被覆の堆積から成る。2つの方法(RF PACVDとRMS)を用いて炭素被覆の適用を行い,異なるパラメータを適用した。インプラント合金の耐食性は,それらの生体適合性の重要な決定因子である。したがって,本研究の目的は,動電位法の使用による孔食に対する抵抗に及ぼす,炭素被覆の種々の適用パラメータを含む,提案した表面改質法の影響を決定することであった。Copyright The Editor(s) (if applicable) and The Author(s), under exclusive license to Springer Nature Switzerland AG 2021 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  電位 ,  *チタン合金 ,  *耐食性 ,  生体適合性 ,  表面改質
準シソーラス用語： 生体材料 ,  擬似体液 ,  機械研磨 ,  カーボンコーティング , 【Automatic Indexing@JST】

著者キーワード (5件)： Ni-Ti合金 ,  生体材料 ,  耐食性 ,  動電位試験 ,  擬似体液

分類 (1件)： 医用素材  (GA05040H)