第5段ガスタービン翼の破壊挙動について【JST・京大機械翻訳】

On the failure behavior of fifth stage gas turbine blade

著者 (5件)： Fallah Sheykhlari Aliakbar (Chemistry and Materials Research Center (CMRC), Metallurgy Department, Niroo Research Institute (NRI), Tehran, Iran) ,  Khani Moghanaki Saeed (Chemistry and Materials Research Center (CMRC), Metallurgy Department, Niroo Research Institute (NRI), Tehran, Iran) ,  Moattari Mastaneh (Chemistry and Materials Research Center (CMRC), Metallurgy Department, Niroo Research Institute (NRI), Tehran, Iran) ,  Shafiei Ali (Chemistry and Materials Research Center (CMRC), Metallurgy Department, Niroo Research Institute (NRI), Tehran, Iran) ,  Amirjan Mostafa (Chemistry and Materials Research Center (CMRC), Metallurgy Department, Niroo Research Institute (NRI), Tehran, Iran)
資料名： Engineering Failure Analysis  (Engineering Failure Analysis)
巻： 116  ページ： Null  発行年： 2020年 
JST資料番号： W0684A  ISSN： 1350-6307  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,500等価運転時間後のガスタービンの5段ブレードの破壊を調べた。ホットガス経路検査の後,ブレードの翼が根から完全に分離されていることが分かった。根の破壊表面を,立体および走査電子顕微鏡(SEM)によって調査した。破面の巨視的研究は疲れ機構が破壊の原因であることを示唆した。ブレードの目視調査は,技術的マップと一致しなかった各ブレード根に小さな溝があることを示した。さらに,溝の寸法は同一ではなく,各ブレードはそれ自身の溝寸法を有した。溝の内側および外側の根の微細構造を調べ,その結果,γ′析出物の形態,サイズおよび分布は溝領域内で変化した。さらに,微細亀裂が溝領域で観察された。得られた結果に従って,溝と微小亀裂(応力集中のポテンシャルサイトとして)の存在が亀裂開始を加速するだけでなく,溝領域内の微細構造変化は溝内の局所化軟化による亀裂核形成に対して相乗効果を持つと結論した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 応力集中 ,  核形成 ,  亀裂 ,  析出物 ,  走査電子顕微鏡 ,  微細構造 ,  *ガスタービン ,  相乗作用 ,  破面 ,  走行時間 ,  亀裂発生 ,  微小亀裂
準シソーラス用語： 局在化 ,  *ガスタービン翼 ,  破壊挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： ブレード ,  ガスタービン ,  疲労 ,  微細構造