Cu-インコネル718粉末混合物の選択的レーザ融解【JST・京大機械翻訳】

Selective laser melting of Cu-inconel 718 powder mixtures

著者 (5件)： Hassanin Andrea El (Department of Chemical, Materials and Production Engineering, University of Napoli Federico II, Piazzale Tecchio 80, Napoli 80125, Italy) ,  Scherillo Fabio (Department of Chemical, Materials and Production Engineering, University of Napoli Federico II, Piazzale Tecchio 80, Napoli 80125, Italy) ,  Prisco Umberto (Department of Chemical, Materials and Production Engineering, University of Napoli Federico II, Piazzale Tecchio 80, Napoli 80125, Italy) ,  Sansone Raffaele (Sophia High Tech, via Romani 228, 80048 Sant’Anastasia, Napoli, Italy) ,  Astarita Antonello (Department of Chemical, Materials and Production Engineering, University of Napoli Federico II, Piazzale Tecchio 80, Napoli 80125, Italy)
資料名： Journal of Manufacturing Processes  (Journal of Manufacturing Processes)
巻： 59  ページ： 679-689  発行年： 2020年 
JST資料番号： W3312A  ISSN： 1526-6125  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 機械的に混合したインコネル718と銅粉末の選択的レーザ融解を,種々のエネルギー入力で異なるCu含有量の原料を処理することによって研究した。Cu含有量の増加とともに,溶融池の幅は減少し,一方,試料の多孔性は増加した。エネルギー入力のより低い値はCu添加によってもたらされる効果を高める。Cu重量分率の減少,あるいは逆に,エネルギー入力の増加,引張および降伏強さは,Cu粉末のような軟質成分の含有量の減少および多孔性の減少の両方により,次第に増加した。多孔性増加のため,原料中の銅含有量の増加に登録された,硬度の減少と熱伝導率の増加は,それぞれ,予想よりも大きく,低い。得られた結果は,Cu-Inconel718混合粉末を用いたSLMによる高密度部品の製造可能性を示した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 熱伝導率 ,  *銅 ,  銅粉 ,  多孔性 ,  溶融池 ,  引張 ,  硬度 ,  *レーザ融解
準シソーラス用語： *Alloy718 ,  高密度 ,  混合粉末 ,  製造可能性 ,  Cu含有量 , 【Automatic Indexing@JST】

著者キーワード (6件)： インコネル718 ,  銅 ,  選択的レーザ融解 ,  空隙率 ,  熱伝導率 ,  エネルギー入力

分類 (2件)： 圧粉,焼結  (WC02030X) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： Cu ,  インコネル718 ,  粉末混合物 ,  レーザ融解