太陽熱エネルギー貯蔵のためのCa(NO_3)_2-NaNO_3-KNO_3システムの熱力学的研究【JST・京大機械翻訳】

Thermodynamic investigation of the Ca(NO₃)₂-NaNO₃-KNO₃ system for solar thermal energy storage

著者 (5件)： Wang Juntao (School of Nuclear Technology and Chemistry & Biology, Hubei University of Science and Technology, Xianning 437100, PR China) ,  Xu Fang (School of Nuclear Technology and Chemistry & Biology, Hubei University of Science and Technology, Xianning 437100, PR China) ,  Hu Yonghong (School of Nuclear Technology and Chemistry & Biology, Hubei University of Science and Technology, Xianning 437100, PR China) ,  Chen Zhiyuan (School of Nuclear Technology and Chemistry & Biology, Hubei University of Science and Technology, Xianning 437100, PR China) ,  Mao Caixia (School of Nuclear Technology and Chemistry & Biology, Hubei University of Science and Technology, Xianning 437100, PR China)
資料名： Thermochimica Acta  (Thermochimica Acta)
巻： 688  ページ： Null  発行年： 2020年 
JST資料番号： E0350C  ISSN： 0040-6031  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 文献で報告されている三成分系Ca(NO_3)_2-NaNO_3-KNO_3の最低液相線温度との混合物の違いを除去するために,共形イオン溶液(CIS)モデルを選択し,この系の相図を予測した。予測結果は,最低液相線温度が116.5°Cである1つの混合物が存在することを示し,その組成は,それぞれ32.4mol%Ca(NO_3)_2+12.4mol%NaNO_3+55.2mol%KNO_3であった。次に,予測した混合物の示差走査熱量測定(DSC)と熱重量分析(TGA)測定を行った。結果は,この塩混合物が115.6±0.1°Cの低融点を有し,予測混合物(116.5°C)の融点と一致し,熱安定性温度は500±1°Cであることを示した。この予測された三成分塩混合物は太陽光発電所のための実行可能な熱エネルギー貯蔵媒体として見ることができる。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 状態図 ,  電解質溶液 ,  *熱力学 ,  三成分系 ,  熱安定性 ,  熱重量分析 ,  融解塩 ,  融点 ,  蓄熱 ,  媒質 ,  液相線 ,  太陽光発電 ,  示差走査熱量測定
準シソーラス用語： *太陽熱エネルギー ,  太陽光発電所 , 【Automatic Indexing@JST】

著者キーワード (4件)： 集光太陽発電 ,  蓄熱 ,  溶融塩 ,  熱力学モデリング

分類 (1件)： 有機物質からなる多成分系の相平衡・状態図  (CB03016J)

タイトルに関連する用語 (5件)： 太陽熱エネルギー ,  貯蔵 ,  Ca ,  熱力学 ,  研究