新しい大気プラズマ溶射AlCoCrFeNi高エントロピー合金マトリックス自己潤滑複合材料被覆の微細構造とトライボロジー挙動【JST・京大機械翻訳】

Microstructure and tribological behavior of a novel atmospheric plasma sprayed AlCoCrFeNi high entropy alloy matrix self-lubricating composite coatings

著者 (17件)： Shi Peiying (State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000, PR China) ,  Shi Peiying (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, 100049, PR China) ,  Yu Yuan (State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000, PR China) ,  Yu Yuan (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, 100049, PR China) ,  Xiong Nina (School of Electronic and Information Engineering, Xi’an Jiaotong University, Xi’an, 710049, PR China) ,  Liu Mingzi (Queen Mary University of London Engineering School, Northwestern Polytechnical University, Xi’an, 710129, PR China) ,  Qiao Zhuhui (State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000, PR China) ,  Qiao Zhuhui (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, 100049, PR China) ,  Yi Gewen (State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000, PR China) ,  Yi Gewen (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, 100049, PR China) ,  Yao Qianqian (State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000, PR China) ,  Yao Qianqian (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, 100049, PR China) ,  Zhao Gaopan (State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000, PR China) ,  Zhao Gaopan (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, 100049, PR China) ,  Xie Erqing (School of Physical Science and Technology, Lanzhou University, Lanzhou, 730000, PR China) ,  Wang Qihua (State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000, PR China) ,  Wang Qihua (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing, 100049, PR China)
資料名： Tribology International  (Tribology International)
巻： 151  ページ： Null  発行年： 2020年 
JST資料番号： E0409B  ISSN： 0301-679X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,AgとBaF_2/CaF_2共晶を有するAlCoCrFeNi高エントロピー合金(HEA)マトリックスコーティングを,大気プラズマ溶射によって首尾よく製造した。種々の温度における溶射したままの被覆のトライボロジー特性を調べた。その結果,潤滑相は典型的なラメラ構造を有する緻密なHEAマトリックス被膜中に均一に分布していることが明らかになった。HEA被覆は,優れた耐摩耗性を示し,さらに,温度上昇とともに改善された。AgとBaF_2/CaF_2共晶の添加は,アブレーション挙動を軽減し,室温で10倍,摩耗速度を著しく減少した。一方,潤滑添加剤は酸化生成物を変化させ,800°Cで酸化物層の剥離を抑制した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 共晶 ,  耐摩耗性 ,  銀 ,  *被覆 ,  *溶射 ,  層状組織 ,  皮膜 ,  アブレーション ,  摩耗速度 ,  *自己潤滑 ,  昇温
準シソーラス用語： トライボロジー特性 ,  *大気プラズマ溶射 ,  *トライボロジー挙動 ,  潤滑添加剤 , 【Automatic Indexing@JST】

著者キーワード (4件)： 高エントロピー合金 ,  大気プラズマ溶射 ,  トライボロジー特性 ,  複合塗料

分類 (1件)： 潤滑一般  (QB02010S)

タイトルに関連する用語 (7件)： 大気プラズマ溶射 ,  高エントロピー合金 ,  マトリックス ,  自己潤滑 ,  複合材料 ,  微細構造 ,  トライボロジー挙動