パルスレーザ誘起溶液ベースナノ製造を理解するための時間的および空間的温度モデリング【JST・京大機械翻訳】

Temporal and spatial temperature modelling for understanding pulsed laser induced solution based nanomanufacturing

著者 (5件)： Liu Siyu ( School of Industrial Engineering (Materials and Manufacturing Group), Purdue University, West Lafayette, Indiana 47907, United States of America) ,  Liu Siyu ( Birck Nanotechnology Center, Purdue University, West Lafayette, Indiana 47907, United States of America) ,  Ou Chun-yu ( School of Industrial Engineering (Materials and Manufacturing Group), Purdue University, West Lafayette, Indiana 47907, United States of America) ,  Liu C. Richard ( School of Industrial Engineering (Materials and Manufacturing Group), Purdue University, West Lafayette, Indiana 47907, United States of America) ,  Liu C. Richard ( Birck Nanotechnology Center, Purdue University, West Lafayette, Indiana 47907, United States of America)
資料名： Nanotechnology  (Nanotechnology)
巻： 31  号： 32  ページ： 325601 (9pp)  発行年： 2020年 
JST資料番号： W0108A  ISSN： 0957-4484  CODEN： NNOTER  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 最近,パルスレーザーは,溶液ベースのナノ製造における標的合成において大きな可能性を示し,空間,時間およびエネルギー入力において高精度および精度を実現した。パルスレーザーにより誘起されたユニークな温度履歴は,関連する基礎を理解し,堆積の精密制御を実現するために不可欠である。本研究では,熱伝達モデルを開発し,反応サイトを横切るパルスレーザー誘起温度変化の時間的発展と空間分布を予測するために適用した。化学的堆積ZnO結晶を例として研究し,レーザパラメータと加熱条件,および蒸着結晶特性の間の関係を示した。パルスレーザーにより誘起されたピーク温度と熱蓄積は,堆積した結晶数密度とサイズに影響を及ぼすことが分かった。核形成数密度分布は,空間温度分布と相関し,結晶サイズに逆比例した。提示した熱伝達モデルは結晶化原理を理解する重要なツールであり,研究,設計,製造および制御のための新しいツールとしてのパルスレーザの促進に不可欠である。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 温度分布 ,  核形成 ,  結晶化 ,  酸化亜鉛 ,  空間分布 ,  *パルスレーザ ,  蓄熱 ,  *パルス ,  温度変動 ,  蒸着 ,  時間発展 ,  密度分布 ,  数密度
準シソーラス用語： *レーザ誘起 ,  温度履歴 , 【Automatic Indexing@JST】

分類 (1件)： 固体デバイス製造技術一般  (NC03030V)

タイトルに関連する用語 (5件)： パルス ,  レーザ誘起 ,  溶液 ,  理解 ,  モデリング