硫黄ガスに対するマグネシア系耐火物の耐食性を評価するための新規で単純な試験の適用【JST・京大機械翻訳】

Application of a novel and simple TEST to evaluate the corrosion resistance of magnesia-based refractories to sulfur gases

著者 (4件)： Fonseca Daniela M. (RHI MAGNESITA Technology Center, Magnesitstrasse 2, 8700, Leoben, Austria) ,  Fonseca Daniela M. (Federal University of Minas Gerais, Engineering School, Department of Metallurgical and Materials Engineering, Avenida Presidente Antonio Carlos, 6627, Belo Horizonte, CEP: 31.270-901, Minas Gerais, Brazil) ,  Gregurek Dean (RHI MAGNESITA Technology Center, Magnesitstrasse 2, 8700, Leoben, Austria) ,  Nunes Eduardo H.M. (Federal University of Minas Gerais, Engineering School, Department of Metallurgical and Materials Engineering, Avenida Presidente Antonio Carlos, 6627, Belo Horizonte, CEP: 31.270-901, Minas Gerais, Brazil)
資料名： Ceramics International  (Ceramics International)
巻： 46  号： 16 PA  ページ： 26160-26167  発行年： 2020年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,硫黄ガスに対する塩基性耐火物の化学抵抗を評価するための新規で簡単な試験を紹介した。この試験は,SO_2/SO_3リッチ雰囲気中での熱処理前後のMgOベース試料の見掛け気孔率とバルク密度の測定に基づいている。これらの性質の変化が大きいほど,耐火物の耐食性が低下することを実証した。この方法を用いて,耐火煉瓦の耐化学性と物理特性に及ぼすCaOのSiO_2(C/S)比の影響を調べた。0.5以下のC/S比の試料は,一次格子間相としてフォルステライト(Mg_2SiO_4)の存在による高い耐食性を示し,これは硫黄ガスと反応しず,マグネシウムと硫酸カルシウムを形成する。このような相の生成は細孔構造のブロッキングを引き起こし,耐火物ライニングの機械的強度を減少させる。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 熱処理 ,  腐食 ,  物理的性質 ,  マグネシウム ,  *耐火物 ,  耐火煉瓦 ,  *耐食性 ,  ライニング ,  *酸化マグネシウム ,  硫酸カルシウム ,  塩基性耐火物 ,  *硫黄 ,  耐化学性 ,  機械的強度
準シソーラス用語： フォルステライト , 【Automatic Indexing@JST】

著者キーワード (4件)： D.MgO ,  C.腐食 ,  E.耐火物 ,  B.微細構造-最終

分類 (1件)： 耐火物  (YC04030N)

タイトルに関連する用語 (6件)： 硫黄 ,  マグネシア ,  耐火物 ,  耐食性 ,  評価 ,  試験