TiC粒子で強化した低合金耐摩耗鋼の凝固と滑り摩耗挙動【JST・京大機械翻訳】

Solidification and sliding wear behavior of low-alloy abrasion-resistant steel reinforced with TiC particles

著者 (6件)： Huang Long (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, 110819, China) ,  Deng Xiangtao (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, 110819, China) ,  Wang Qi (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, 110819, China) ,  Jia Ye (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, 110819, China) ,  Li Chengru (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, 110819, China) ,  Wang Zhaodong (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, 110819, China)
資料名： Wear  (Wear)
巻： 458-459  ページ： Null  発行年： 2020年 
JST資料番号： E0377A  ISSN： 0043-1648  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 自己生成TiC粒子で強化した低合金耐摩耗性鋼を開発し,その硬度を増加させずに摩耗性能を改善した。凝固実験を行い,ミクロンサイズのTiC粒子のサイズ,含有量および分布に及ぼすTiおよび凝固速度の質量比の影響を調べた。種々の負荷荷重の下で異なる凝固速度で製造したTiの異なる質量分率を有するTiC強化鋼の滑り摩耗挙動を,乾燥滑り摩耗試験機を用いて研究した。結果は,TiC強化鋼のミクロ組織がマルテンサイト/ベイナイトマトリックスとミクロンサイズのTiC粒子から成ることを示した。Ti質量分率と凝固速度の増加に伴い,TiC粒子の数は増加する。異なる負荷の下で,凝固速度3~°C/minで作製したTiC強化鋼は,最良の滑り摩耗性能を示した。摩耗形態とEDSマップは,TiC強化鋼の乾燥滑り摩耗の主な摩耗機構が酸化摩耗とアブレシブ摩耗であることを示した。摩耗表面の断面形態は,ミクロンサイズの粒子がマトリックスを摩耗から保護し,変形に対するマトリックスの抵抗を強化することを明らかにした。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *凝固 ,  *摩耗 ,  *チタン ,  *鋼 ,  マルテンサイト ,  *耐摩耗鋼 ,  凝固速度 ,  アブレシブ摩耗 ,  摩耗特性 ,  *滑り摩耗
準シソーラス用語： 摩耗面 ,  摩耗機構 ,  腐食摩耗 ,  乾燥滑り摩耗 ,  *摩耗挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： TiC粒子 ,  凝固 ,  低合金耐摩耗鋼 ,  滑り摩耗