黄銅-アンバ熱バイメタルにおける界面の構造に及ぼす爆発溶接パラメータの影響【JST・京大機械翻訳】

Influence of Explosive Welding Parameters on the Structure of Interface in Brass-Invar Thermobimetal

著者 (5件)： Saikov I. V. (Merzhanov Institute of Structural Macrokinetics and Materials Science, Russian Academy of Sciences, Chernogolovka, Russia) ,  Malakhov A. Yu. (Merzhanov Institute of Structural Macrokinetics and Materials Science, Russian Academy of Sciences, Chernogolovka, Russia) ,  Saikova G. R. (Merzhanov Institute of Structural Macrokinetics and Materials Science, Russian Academy of Sciences, Chernogolovka, Russia) ,  Denisov I. V. (Merzhanov Institute of Structural Macrokinetics and Materials Science, Russian Academy of Sciences, Chernogolovka, Russia) ,  Gulyaev P. Yu. (Yugra State University, Khanty-Mansiysk, Russia)
資料名： Inorganic Materials: Applied Research  (Inorganic Materials: Applied Research)
巻： 11  号： 2  ページ： 448-452  発行年： 2020年 
JST資料番号： W4443A  ISSN： 2075-1133  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 層の品質と熱バイメタルグレードTB1353(TB130/17)の溶接部の構造に及ぼすInvar36Nを有する黄銅L63の爆発溶接の運動学的パラメータの影響を実験的に研究した。熱バイメタル中の活性層として,溶融性成分(亜鉛)を含む合金L63を用いるので,「放出」効果の防止を考慮して溶接モードの選択を行うべきであることを示した。この場合,高圧で衝撃圧縮されたガスの流れは,高速度でギャップを移動し,低融点を運ぶ。したがって,接合部の強度は,強度の完全な損失まで減少し,また,溶接部の層の相(化学的)均一性も破れた。熱バイメタルの継手を超音波流検出器で試験した。溶接部の構造を光学顕微鏡と電子顕微鏡により調べた。破断中の層の靭性をリング試料で測定した。クラッド層の横曲げと曲げに関する試験を実施した。接着層の100%の連続性を有する固相における爆発的溶接を提供する最適モードと黄銅の強度のレベルでの破壊の間の層の靱性と溶接部の高品位構造を決定した。Copyright Pleiades Publishing, Ltd. 2020 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *界面 ,  高圧 ,  超音波 ,  電子顕微鏡 ,  電子顕微鏡観察 ,  破断 ,  *黄銅 ,  光学顕微鏡 ,  *溶接 ,  *爆発圧接 ,  溶接部 ,  靱性 ,  *アンバ ,  活性層
準シソーラス用語： 高品質 ,  接着層 , 【Automatic Indexing@JST】

著者キーワード (5件)： 爆発溶接 ,  バイメタル ,  界面 ,  衝撃圧縮ガス ,  熱静的バイメタル

分類 (2件)： 溶接技術  (WC07030G) ,  クラッド材  (WE04020G)

タイトルに関連する用語 (6件)： 黄銅 ,  アンバ ,  バイメタル ,  界面 ,  爆発溶接 ,  パラメータ