液体複合材料成形-熱分解プロセスによる低空隙率のSiC_f/SiC複合材料の調製【JST・京大機械翻訳】

Preparation of SiC_f/SiC Composites with Low Porosity by Liquid Composite Moulding-Pyrolysis Process

著者 (10件)： Wang Xiaomeng (AVIC Aviation Foundation Technology Establishment, Beijing 101300, China) ,  Wang Xiaomeng (AVIC Composite Co., Ltd, Beijing 101300, China) ,  Zhang Bingyu (AVIC Aviation Foundation Technology Establishment, Beijing 101300, China) ,  Zhang Bingyu (AVIC Composite Co., Ltd, Beijing 101300, China) ,  Zhao Yuliang (AVIC Aviation Foundation Technology Establishment, Beijing 101300, China) ,  Zhao Yuliang (AVIC Composite Co., Ltd, Beijing 101300, China) ,  Wang Ling (AVIC Aviation Foundation Technology Establishment, Beijing 101300, China) ,  Wang Ling (AVIC Composite Co., Ltd, Beijing 101300, China) ,  Qiu Haipeng (AVIC Aviation Foundation Technology Establishment, Beijing 101300, China) ,  Qiu Haipeng (AVIC Composite Co., Ltd, Beijing 101300, China)
資料名： IOP Conference Series: Materials Science and Engineering  (IOP Conference Series: Materials Science and Engineering)
巻： 678  号： 1  ページ： 012056 (7pp)  発行年： 2019年 
JST資料番号： W5559A  ISSN： 1757-8981  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 伝統的に,高分子浸透と熱分解(PIP),化学蒸気浸透(CVI)および溶融浸透(MI)は,魅力的な潜在的高温構造材料の一つである連続炭化ケイ素繊維強化炭化ケイ素マトリックス(SiC_f/SiC)複合材料を製造する主なプロセスである。しかし,長い調製期間と高い空隙率は,更なる応用のためにまだ問題である。特に,気孔率は機械的性質に重要である。液体複合材料成形-熱分解(LCMP)は,液体SiC前駆体を用いて,11サイクルの溶浸と熱分解を伴わずに,開放気孔率を5%まで減少させた。曲げ強さのような機械的性質を異なる厚さの熱分解炭素(PyC)界面と熱分解サイクルで調べた。1200°Cの熱分解温度下で200nmのPyC界面で曲げ強度は585MPaに達した。したがって,LCMPプロセスは,SiC_f/SiC複合材料の性能を改善するための刺激的機会を提供する。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  CVI【浸透】 ,  *熱分解 ,  溶浸 ,  高分子 ,  複合材料 ,  浸透 ,  *炭化ケイ素 ,  機械的性質 ,  高温 ,  空隙率 ,  炭化ケイ素系繊維 ,  構造材料 ,  曲げ強さ ,  前駆体 ,  性質 ,  強度