GGG単結晶の亀裂のない研削の変形特性と表面生成モデリング【JST・京大機械翻訳】

Deformation characteristics and surface generation modelling of crack-free grinding of GGG single crystals

著者 (7件)： Li Chen (School of Mechatronics Engineering, Harbin Institute of Technology, Harbin, 150001, China) ,  Li Chen (School of Mechanical and Mining Engineering, University of Queensland, QLD 4072, Australia) ,  Wu Yueqin (Institute of Manufacturing Engineering, Huaqiao University, Xiamen, 361021, China) ,  Li Xuliang (School of Mechanical and Mining Engineering, University of Queensland, QLD 4072, Australia) ,  Ma Lianjie (School of Control Engineering, Northeastern University at Qinhuangdao, Qinhuangdao, 066004, China) ,  Zhang Feihu (School of Mechatronics Engineering, Harbin Institute of Technology, Harbin, 150001, China) ,  Huang Han (School of Mechanical and Mining Engineering, University of Queensland, QLD 4072, Australia)
資料名： Journal of Materials Processing Technology  (Journal of Materials Processing Technology)
巻： 279  ページ： Null  発行年： 2020年 
JST資料番号： H0650A  ISSN： 0924-0136  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ガリウムガドリニウムガーネット(GGG)単結晶は,高出力固体レーザを作るための主要なホスト材料である。GGG単結晶は,それらの高い硬度と脆性のために,困難な機械材料である。GGG結晶の超精密研削実験を行い,脆性破壊と亀裂の表面と表面下の自由表面を発生させた。TEM試験は,超精密研削により誘起されたGGG結晶の塑性形成が,(114)結晶面のすべり,ならびにナノ結晶化と非晶質化により支配されることを示した。表面の形態と粗さをAFMで測定した。研磨砥粒の半径,位置および突起高さのランダム分布を考慮することにより,表面形態および表面粗さを予測するための理論モデルを開発した。シミュレーション結果は実験と良く一致した。このように,このモデルは,硬質および脆性結晶の超精密研削における表面仕上げに及ぼす材料変形および除去の影響を理解するために有用であり,そして,硬質および脆性結晶の研削のプロセスパラメータを最適化するための意味ある指針を提供することができた。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 固体レーザ ,  *単結晶 ,  結晶面 ,  プロセスパラメータ ,  アモルファス化 ,  表面仕上 ,  砥粒 ,  最適化 ,  脆性破壊 ,  *研削 ,  *結晶 ,  脆性 ,  シミュレーション ,  *亀裂 ,  塑性

著者キーワード (6件)： GGG単結晶 ,  研削 ,  変形 ,  表面粗さ ,  シミュレーション ,  モデル