GdNb_1-xW_xO_4+δ新規灰重石型酸化物イオン伝導体の合成と試験【JST・京大機械翻訳】

Synthesis and examination of GdNb_1-x W _x O_4+δ new scheelite-type oxide-ion conductor

著者 (5件)： Kawaguchi Ryo (Department of Fundamental Engineering, School of Engineering, Utsunomiya University, 7-1-2 Yoto, Utsunomiya 321-8585, Japan) ,  Akizawa Ryoji (Department of Fundamental Engineering, School of Engineering, Utsunomiya University, 7-1-2 Yoto, Utsunomiya 321-8585, Japan) ,  Shan Yue Jin (Department of Fundamental Engineering, School of Engineering, Utsunomiya University, 7-1-2 Yoto, Utsunomiya 321-8585, Japan) ,  Tezuka Keitaro (Department of Fundamental Engineering, School of Engineering, Utsunomiya University, 7-1-2 Yoto, Utsunomiya 321-8585, Japan) ,  Katsumata Tetsuhiro (Department of Chemistry, School of Science, Tokai University, 4-1-1 Kitakaname, Hiratsuka-shi, Kanagawa 259-1292, Japan)
資料名： Solid State Ionics  (Solid State Ionics)
巻： 355  ページ： Null  発行年： 2020年 
JST資料番号： B0096B  ISSN： 0167-2738  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Nbに対するW置換による新しい固溶体系GdNb_1-xW_xO_4+δの合成を固相反応法によって調べた。系の構造は,W置換の増加と共に単斜晶フェルグソナイト相から正方晶灰重石相に変化し,単一正方晶灰重石相が0.3≦x≦0.7の組成で室温で得られることが分かった。構造相転移温度はW置換の増加と共に減少し,正方晶灰重石相はW置換により安定化され,シンクロトロン粉末X線回折により明らかになった。GdNbO_4の伝導率は,Nbに対するWの置換により著しく改善され,GdNb_1-xW_xO_4+δ(0.4≦x≦0.6)試料は,600°Cの中間温度で10-5Scm-1に達した。置換試料の伝導率の活性化エネルギーは温度とW置換量に関係なくほぼ一定であった。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 活性化エネルギー ,  固相反応 ,  固溶体 ,  シンクロトロン ,  転移温度 ,  *ニオブ ,  *灰重石 ,  単斜晶系 ,  正方晶系 ,  構造相転移
準シソーラス用語： 粉末X線回折 ,  *酸化物イオン ,  中間温度 ,  酸化物イオン伝導体 ,  伝導率 , 【Automatic Indexing@JST】

著者キーワード (5件)： W置換 ,  構造相転移 ,  格子間酸化物イオン ,  灰重石型構造 ,  酸化物イオン伝導体