アーク溶接によるパルスアーク光モニタリングと温度再構成【JST・京大機械翻訳】

Pulsed arc light monitoring and temperature reconstruction with arc welding

著者 (5件)： Mingxuan Yang (Department Materials Processing, School of Mechanical Engineering and Automation, Beijing University of Aeronautics and Astronautics, Beijing, People’s Republic of China) ,  Hao Zheng (Department Materials Processing, School of Mechanical Engineering and Automation, Beijing University of Aeronautics and Astronautics, Beijing, People’s Republic of China) ,  Bojin Qi (Department Materials Processing, School of Mechanical Engineering and Automation, Beijing University of Aeronautics and Astronautics, Beijing, People’s Republic of China) ,  Zhexu Wang (Department Aeronautics and Astronautics, University of Tokyo, Tokyo, Japan) ,  Rainy Liu (BIM, Honeywell Technology Solution China (HTSC), R&D Honeywell, Beijing, People’s Republic of China)
資料名： Science and Technology of Welding and Joining  (Science and Technology of Welding and Joining)
巻： 25  号： 7  ページ： 535-542  発行年： 2020年 
JST資料番号： W1175A  ISSN： 1362-1718  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ABSTRACT:過渡パルスアークを狭帯域696.5nmフィルタで研究した。アークエネルギー分布を比:ある領域エネルギー(強度×領域面積)/和によって考慮した。その結果,パルスアークで大きな強度領域が現れ,高エネルギー領域と考えられた。低エネルギー領域が圧縮された間,それらは増加した。分布比は,大電流またはパルスアークによるΔΣ波ラッシュパターンによって変化した。鋭いエネルギー濃度はアークの底部で見出された。100Aの10kHzのパルスアークは,形状およびエネルギー分布において最適特性を有した。パルスアークの本質を収縮エネルギー領域として考慮し,高エネルギー密度を生成した。アーク強度を再構成するために,ΔΣOnion-Kasugaアルゴリズムを提案した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： アルゴリズム ,  フィルタ ,  *アーク溶接 ,  パルスアーク溶接 ,  エネルギー分布 ,  再構成 ,  エネルギー領域 ,  *パルス ,  高エネルギー領域 ,  低エネルギー領域 ,  狭帯域
準シソーラス用語： 大電流 , 【Automatic Indexing@JST】

著者キーワード (3件)： パルスアーク溶接 ,  アーク光 ,  温度再構成

分類 (1件)： 溶接技術  (WC07030G)