シリカフュームスラグ無機ポリマーの初期性能に関する研究【JST・京大機械翻訳】

Study on the early performance of silica fume-slag inorganic polymer

著者 (6件)： Zhang Hengbo (National Defense Engineering Institute, Academy of Military Sciences, Beijing, 100036, China) ,  Xu Jinyu (Teaching-research Office of Airfield and Building Engineering, Air Force Engineering University, Xi’an, Shanxi 710038, China) ,  Xu Jinyu (College of Mechanics and Civil Architecture, Northwest Polytechnic University, Xi’an, Shanxi, 710072, China) ,  Luo Xin (National Defense Engineering Institute, Academy of Military Sciences, Beijing, 100036, China) ,  Yu Huang (National Defense Engineering Institute, Academy of Military Sciences, Beijing, 100036, China) ,  Nie Liangxue (93125 troops of PLA, Xuzhou, Jiangsu, 221005, China)
資料名： IOP Conference Series: Earth and Environmental Science  (IOP Conference Series: Earth and Environmental Science)
巻： 510  号： 5  ページ： 052035 (7pp)  発行年： 2020年 
JST資料番号： W5558A  ISSN： 1755-1307  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： スラグ無機ポリマーに基づき,それぞれ5%,10%,15%,20%,25および30%の通常および半高密度シリカフュームスラグ含有量を有するシリカフュームスラグ無機ポリマー(SSIP)を調製し,SIPの作動性能,初期機械的性質および相を研究した。その結果,2種類のシリカフュームは,SIPの初期および最終凝結時間をある程度延長し,作動性能を改善するが,全体として,シリカフュームの添加は,圧縮および曲げ強度を弱め,従って,初期機械的特性を低下させる,ことが分ったが,そのために,シリカフュームの添加は,圧縮および曲げ強度を弱め,そして,全体として,シリカフュームの添加は,圧縮および曲げ強度を弱めた。SSIPのXRDスペクトルは,シリカフュームを添加した後に明らかな変化を持たず,2種類のSIPの相組成は類似し,シリカフューム含有量が大きいほど,SIPの非晶質含有量は高かった。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  機械的性質 ,  *スラグ ,  X線回折分析 ,  *無機重合体 ,  非晶質 ,  スペクトル ,  相組成 ,  *シリカヒューム
準シソーラス用語： 高密度 ,  凝結時間 , 【Automatic Indexing@JST】

分類 (1件)： モルタル,コンクリート  (RA06042H)

タイトルに関連する用語 (3件)： 無機ポリマー ,  初期 ,  研究