Zr基バルク金属ガラスの選択的レーザ融解における過渡核形成【JST・京大機械翻訳】

Transient nucleation in selective laser melting of Zr-based bulk metallic glass

著者 (7件)： Ericsson A. (Division of Solid Mechanics, Lund University, PO Box 118, SE 22100 Lund, Sweden) ,  Pacheco V. (Department of Chemistry, Ångstrom Laboratory, Uppsala University, Box 523, SE 75120 Uppsala, Sweden) ,  Sahlberg M. (Department of Chemistry, Ångstrom Laboratory, Uppsala University, Box 523, SE 75120 Uppsala, Sweden) ,  Lindwall J. (Mechanics of Solid Materials, Lulea Technical University, SE 97187 Lulea, Sweden) ,  Hallberg H. (Division of Solid Mechanics, Lund University, PO Box 118, SE 22100 Lund, Sweden) ,  Fisk M. (Division of Solid Mechanics, Lund University, PO Box 118, SE 22100 Lund, Sweden) ,  Fisk M. (Materials Science and Applied Mathematics, Malmo University, SE 20506 Malmo, Sweden)
資料名： Materials & Design  (Materials & Design)
巻： 195  ページ： Null  発行年： 2020年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： バルク金属ガラス(BMG)の選択的レーザ融解(SLM)中の結晶化速度は,材料の非晶質構造の維持における重要因子である。SLMプロセスとBMGの結晶化挙動の間の相互作用の理解を増すために,SLMに関連する急速温度変化を説明する古典的核形成理論に基づく数値モデルを開発した。このモデルをZr基BMGのSLMに適用し,このモデルによって説明される過渡的効果は,冷却時の定常状態核形成速度より15桁まで核形成速度を低下させ,その結果,構築過程でより少ない核となることを示した。提案したモデリング手法の能力を,得られた結晶体積分率を実験結果と比較することによって実証した。モデル予測と実験結果との一致は,BMGsのSLM処理中の結晶化速度を考慮する場合,過渡的核形成効果が考慮されるべきであることを明瞭に示唆した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *核形成 ,  結晶化 ,  相互作用 ,  *ジルコニウム ,  温度変動 ,  晶析速度 ,  *レーザ融解 ,  *金属ガラス ,  *バルク金属ガラス ,  付加製造
準シソーラス用語： 核形成速度 ,  数値モデル ,  定常状態 ,  非晶質構造 ,  モデル予測 , 【Automatic Indexing@JST】

著者キーワード (6件)： 付加製造 ,  選択的レーザ融解 ,  金属ガラス ,  結晶化 ,  古典的核形成理論 ,  過渡核形成

分類 (3件)： 圧粉,焼結  (WC02030X) ,  鋳造に関する各種技術  (WC01040B) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： Zr ,  バルク金属ガラス ,  レーザ融解 ,  核形成