水素化チタン粉末における酸化誘起立方晶-正方晶相変態【JST・京大機械翻訳】

Oxidation induced cubic-tetragonal phase transformation in titanium hydride powders

著者 (7件)： Ben David R. (Department of Materials Science and Engineering, Technion - Israel Institute of Technology, 3200003, Haifa, Israel) ,  Ben David R. (Israel Atomic Energy Commission, P.O. Box 7061, 61070, Tel Aviv, Israel) ,  Finkelstein Y. (Nuclear Research Center Negev, P.O. Box 9001, 84190, Beer-Sheva, Israel) ,  Grinberg E. (Nuclear Research Center Negev, P.O. Box 9001, 84190, Beer-Sheva, Israel) ,  Samuha S. (Nuclear Research Center Negev, P.O. Box 9001, 84190, Beer-Sheva, Israel) ,  Rabkin E. (Department of Materials Science and Engineering, Technion - Israel Institute of Technology, 3200003, Haifa, Israel) ,  Cohen D. (Nuclear Research Center Negev, P.O. Box 9001, 84190, Beer-Sheva, Israel)
資料名： International Journal of Hydrogen Energy  (International Journal of Hydrogen Energy)
巻： 45  号： 46  ページ： 25043-25053  発行年： 2020年 
JST資料番号： B0192B  ISSN： 0360-3199  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 空気中の水素化チタン粉末の熱酸化により誘起された立方晶(δ)から正方晶(ε)相変態への酸化温度と初期水素濃度の影響を調べた。X線回折分析は,δ→ε変態が400°Cでの酸化時に起こるが,より低い(300°C)あるいはより高い(500°C)酸化温度では起こらないことを示した。酸化中の水素損失の相対量を温度プログラム脱着質量分析(TPD-MS)により決定した。この知見は,酸素が正方晶相(ε)を安定化し,酸化後のδ/ε相組成が酸素と水素濃度の両方に依存することを示唆する。高い酸化温度(500°C)では,ある程度の水素化物分解が,室温まで冷却後,H濃度の減少と正方晶相の不安定化につながった。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  *酸化 ,  質量分析 ,  *粉体 ,  酸素 ,  *水素 ,  X線回折分析 ,  水素化物 ,  相組成 ,  *立方晶系 ,  *正方晶系 ,  昇温脱離 ,  熱酸化
準シソーラス用語： *水素化チタン ,  水素濃度 , 【Automatic Indexing@JST】

著者キーワード (6件)： 水素化チタン(TiH_2) ,  相変態 ,  酸化 ,  X線回折 ,  昇温脱離 ,  質量分析(TPD-MS)

分類 (2件)： その他の金属組織学  (WB01040Y) ,  気体燃料の輸送,供給,貯蔵  (YE02060M)

タイトルに関連する用語 (7件)： 水素化チタン ,  粉末 ,  酸化 ,  誘起 ,  立方晶 ,  正方晶 ,  相変態