PHSレーザ溶接中の溶融領域の微細構造に及ぼすNi箔厚さの影響【JST・京大機械翻訳】

Effect of Ni foil thickness on the microstructure of fusion zone during PHS laser welding

著者 (7件)： Wang Xiaonan (Shagang School of Iron and Steel, Soochow University, Suzhou 215021, PR China) ,  Zhang Zhenghui (Shagang School of Iron and Steel, Soochow University, Suzhou 215021, PR China) ,  Hu Zengrong (School of Urban Rail Transportation, Soochow University, Suzhou 215021, PR China) ,  Sun Qian (State Key Laboratory of Rolling and Automation of Northeastern University, Shenyang 110819, PR China) ,  Di Hongshuang (State Key Laboratory of Rolling and Automation of Northeastern University, Shenyang 110819, PR China) ,  Lv Fan (Shagang School of Iron and Steel, Soochow University, Suzhou 215021, PR China) ,  Sun Lining (School of Mechanical and Electric Engineering, Soochow University, Suzhou 215021, PR China)
資料名： Optics & Laser Technology  (Optics & Laser Technology)
巻： 125  ページ： Null  発行年： 2020年 
JST資料番号： D0245B  ISSN： 0030-3992  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,1.5mm厚さの熱間圧延Al-Si被覆プレス硬化鋼(PHS)を,中間層としてNi箔を用いてレーザテーラー溶接した。融合領域(FZ)の微細構造進展に及ぼすNi箔厚さの影響を研究した。Ni箔の厚さが増加すると,AlはFZにおいて均一なプロフィルを有したが,Niは融合境界に偏析を有した。JMatPro分析結果は,高温でのδ-フェライトの割合が減少し,一次凝固相がδ-フェライトからγ相に変化することを示した。溶融境界とFZ中心は,レーザ溶接の間,類似の凝固相進化を有した。Ni箔が30μmのとき,微細構造はδ-フェライトとラスマルテンサイトの組成であったが,Ni箔を有する完全マルテンサイトは60μmまで増加した。オーステナイトは100μmに増加したNi箔との融合境界に存在したが,それはFZ中心においてまだラスマルテンサイトであった。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： アルミニウム ,  オーステナイト ,  *レーザ溶接 ,  γ相 ,  *ニッケル ,  凝固 ,  フェライト ,  高温 ,  *溶接 ,  焼入鋼 ,  熱間圧延 ,  マルテンサイト ,  被覆 ,  偏析
準シソーラス用語： ラスマルテンサイト , 【Automatic Indexing@JST】

著者キーワード (6件)： 溶接 ,  デルタフェライト ,  Al-Si被覆 ,  オーステナイト ,  プレス硬化鋼 ,  相変態

分類 (2件)： レーザの応用  (BD04100V) ,  溶接技術  (WC07030G)

タイトルに関連する用語 (7件)： PHS ,  レーザ溶接 ,  溶融領域 ,  微細構造 ,  Ni ,  箔 ,  厚さ