亜共晶Al-7%Si合金のミクロ組織および機械的性質に及ぼすFe,MnおよびY添加の影響【JST・京大機械翻訳】

Influences of Fe, Mn and Y additions on microstructure and mechanical properties of hypoeutectic Al-7%Si alloy

著者 (16件)： Li Qinglin (School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Li Qinglin (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Zhu Yuqian (School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Zhu Yuqian (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Zhao Shang (School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Zhao Shang (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Lan Yefeng (School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Lan Yefeng (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Liu Dexue (School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Liu Dexue (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Jian Guangfei (School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Jian Guangfei (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Zhang Qiang (School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Zhang Qiang (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Zhou Hongwei (School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050, China) ,  Zhou Hongwei (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China)
資料名： Intermetallics  (Intermetallics)
巻： 120  ページ： Null  発行年： 2020年 
JST資料番号： W0672A  ISSN： 0966-9795  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,亜共晶Al-7%Si合金のミクロ組織変化および機械的性質に及ぼす種々の含有量のFe,MnおよびYの影響を,顕微鏡技術および引張試験によって調査した。結果は,Al-20%Si-2.5%Fe-2%Mn母合金と希土類Yの複雑な添加が,母合金または希土類Yの別々の添加よりも,より良い微細化効果を有することを示した。7.0%母合金と0.2%Yの組合せ添加により,平均粒径は483.1μmから50.8μmへ89.5%減少し,二次デンドライトアーム間隔(SDAS)は26.9μmから14.3μmへ46.8%減少した。さらに,粗いフレーク状共晶Si構造は微細繊維と粒状形状に効果的に改質された。加えて,極限引張強さ(UTS)は162MPaから216MPaまで33.3%改善され,伸び(El)値は6.2%から9.1%まで46.7%まで強化された。破壊モードは脆性破壊から延性破壊に変化した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *共晶 ,  *合金 ,  引張強さ ,  微細繊維 ,  機械的性質 ,  母合金 ,  樹枝状結晶 ,  *ケイ素 ,  希土類元素 ,  延性破壊 ,  フレーク ,  *ケイ素合金 ,  脆性破壊 ,  破壊モード ,  引張試験

著者キーワード (6件)： 亜共晶Al-7%Si合金 ,  微細構造 ,  Al-20%Si-2.5%Fe-2%Mn母合金 ,  希土類Y ,  機械的性質 ,  金属間合金