累積ロールボンディングプロセスにより作製したNi/Ti多層複合材料の構造と機械的性質【JST・京大機械翻訳】

Structure and mechanical properties of Ni/Ti multilayered composites produced by accumulative roll-bonding process

著者 (5件)： Mokhles Mohammad (Department of Materials Science and Engineering, School of Engineering, Shiraz University, Iran) ,  Hosseini Morteza (Department of Materials Science and Engineering, School of Engineering, Shiraz University, Iran) ,  Hosseini Morteza (Department of Mechanical Engineering, Faculty of Engineering, University of Hormozgan, Iran) ,  Danesh-Manesh Habib (Department of Materials Science and Engineering, School of Engineering, Shiraz University, Iran) ,  Zebarjad Seyed Mojtaba (Department of Materials Science and Engineering, School of Engineering, Shiraz University, Iran)
資料名： Journal of Composite Materials  (Journal of Composite Materials)
巻： 54  号： 8  ページ： 1119-1126  発行年： 2020年 
JST資料番号： B0859A  ISSN： 0021-9983  CODEN： JCOMB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,商用純NiとTi箔から製造したNi/Ti多層複合材料の構造と機械的性質を,累積ロールボンディング法により研究した。これらの特性を調べるために,走査電子顕微鏡,Vickers微小硬さ,および一軸引張試験を異なる処理サイクルで行った。研究は,構造に関して,NiとTi層が,10サイクルまでの累積ロール結合においてさえ,それらの連続性を維持することを示した。さらに,走査電子顕微鏡におけるエネルギー分散分光法は,変形誘起拡散または反応性界面ゾーンを検出しなかった。累積ロール結合サイクル,引張および降伏強度の増加により,複合材料の硬さと同様に引張および降伏強さが増加し,全伸びが連続的に減少することが分かった。Copyright The Author(s) 2019 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 引張 ,  界面 ,  降伏強さ ,  走査電子顕微鏡 ,  多層 ,  *チタン ,  複合材料 ,  硬度 ,  *機械的性質 ,  *ニッケル ,  連続性
準シソーラス用語： エネルギー分散分光法 ,  一軸引張試験 ,  Vickers微小硬さ ,  *ロール圧接 , 【Automatic Indexing@JST】

著者キーワード (5件)： Ni/Ti多層複合材料 ,  累積ロールボンディング ,  構造 ,  硬さ ,  引張特性