シールド金属アーク溶接(SMAW)を用いた異なるタイプの溶接継手の腐食速度の研究【JST・京大機械翻訳】

Investigation of Corrosion Rate for Different Type of Welding Joints using Shielded Metal Arc Welding (SMAW)

著者 (5件)： Sulaiman S. A. (Faculty of Mechanical Engineering, University Teknologi MARA (UiTM) Kampus Pasir Gudang 81750 Masai Johor Malaysia) ,  Abdullah B. (Faculty of Mechanical Engineering, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor Malaysia) ,  Alias S. K. (Faculty of Mechanical Engineering, University Teknologi MARA (UiTM) Kampus Pasir Gudang 81750 Masai Johor Malaysia) ,  Ahmad N. N. (Faculty of Mechanical Engineering, University Teknologi MARA (UiTM) Kampus Pasir Gudang 81750 Masai Johor Malaysia) ,  Aziz M. N. A (Faculty of Mechanical Engineering, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor Malaysia)
資料名： IOP Conference Series: Materials Science and Engineering  (IOP Conference Series: Materials Science and Engineering)
巻： 834  号： 1  ページ： 012055 (7pp)  発行年： 2020年 
JST資料番号： W5559A  ISSN： 1757-8981  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 腐食は金属とその周囲の化学反応の結果として金属の劣化である。異なるタイプの金属と環境条件,特に金属と接触するガスは腐食の速度を決定する。異なるタイプの溶接継手は,通常,塩,空気,水,材料組成,流体中の溶存酸素量,pHおよび流体の速度特性のような腐食およびエロージョン剤に暴露される種々のタイプの溶接継手から,腐食問題に寄与する因子である。塩化ナトリウム(NaCl),塩酸(HCl),蒸留水および天然海水に30~50日間浸漬した後に,突合せ継手,重ね継手および端部継手である3種類の溶接継手における軟鋼の腐食速度を調べるために研究を行った。軟鋼は,シールド金属アーク溶接を用いて接合した。溶接継手の各々に対して,電流,電圧および走行速度であるパラメータを固定した。浸漬と硬度試験を行って腐食速度を識別した。その結果,突合せ継手は重ね継手および端部継手よりも高い腐食速度を示し,腐食過程中に形態変態差が生じた。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 硬さ試験 ,  電圧 ,  電流 ,  *腐食 ,  化学反応 ,  軟鋼 ,  *腐食速度 ,  *アーク溶接 ,  *溶接継手 ,  走行速度 ,  塩化ナトリウム ,  塩酸 ,  重ね継手