3D印刷ABSの引張及び圧縮特性に及ぼす層厚及び断面形状の影響【JST・京大機械翻訳】

Effect of layer thickness and cross-section geometry on the tensile and compression properties of 3D printed ABS

著者 (6件)： Nomani Junior (Faculty Office of Design and Creative Technologies, Mechanical Engineering Department, AUT University, Auckland, New Zealand) ,  Wilson Daniel (School of Engineering, Deakin University, Waurn Ponds, Australia) ,  Paulino Mariana (School of Engineering, Deakin University, Waurn Ponds, Australia) ,  Mohammed Mazher Iqbal (School of Engineering, Deakin University, Waurn Ponds, Australia) ,  Mohammed Mazher Iqbal (School of Medicine, Deakin University, Waurn Ponds, Australia) ,  Mohammed Mazher Iqbal (School of Design and Creative Arts, Loughborough University, Loughborough, UK)
資料名： Materials Today Communications  (Materials Today Communications)
巻： 22  ページ： Null  発行年： 2020年 
JST資料番号： W3060A  ISSN： 2352-4928  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,FFFを用いた製造時の印刷ABS材料の機械的性質に及ぼす堆積層厚の影響を調べた。引張と圧縮試験を,0.2mmと0.8mmの間の層厚で印刷されたサンプルに関するASTM規格に対して実行した。結果は,材料強度と剛性が,σy(0.8mm)=23.0MPa,UTS0.8mm=31.0MPaと比較して,より小さい層厚さ,例えばσy(0.2mm)=31.5MPa,UTS0.2mm=38.2MPa,を用いて最大であることを見出した。機械的性質における記録された変化は,製造残留気孔率,層間結合強度を促進する堆積層の数,および材料剪断硬化をもたらす押出プロセスに関連する機構によって説明される。これらの知見は,材料堆積の増加の方法を用いて全体的な部品プリント時間を低減する能力に関する意味を有し,非改質ABSポリマによる大量の堆積印刷フォーマットを利用するとき,比較部品の完全性に大きな意味を持つ可能性がある。また,本研究からの知見は,3D印刷材料の試験のための適切なガイドラインに適合するための現在の機械的試験規格の必要性を強調し,層の厚さとプリント形状に基づいて測定された引張と圧縮特性の広い分散を与えた。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 高分子 ,  空隙率 ,  規格 ,  機械的性質 ,  *印刷 ,  圧縮性 ,  圧縮試験 ,  *引張 ,  *層厚 ,  剪断 ,  剛性 ,  ASTM規格 ,  完全性 ,  機械的検査
準シソーラス用語： *三次元印刷 , 【Automatic Indexing@JST】

著者キーワード (5件)： 層厚 ,  層の高さ ,  FFF ,  層間結合強度 ,  高分子硬化

分類 (3件)： 強化プラスチックの成形  (YH04060J) ,  炭素とその化合物  (YB02060D) ,  機械的性質  (YH02022L)

タイトルに関連する用語 (6件)： 3D印刷 ,  ABS ,  引張 ,  圧縮特性 ,  層厚 ,  断面形状