中性子照射U(Mo)におけるナノバブル格子の初期形成段階【JST・京大機械翻訳】

The initial formation stages of a nanobubble lattice in neutron irradiated U(Mo)

著者 (7件)： Salvato D. (SCK・CEN, Nuclear Materials Science Institute, Boeretang 200, 2400, Mol, Belgium) ,  Salvato D. (Ghent University, Department of Solid State Sciences, Krijgslaan 281/S1, 9000, Ghent, Belgium) ,  Leenaers A. (SCK・CEN, Nuclear Materials Science Institute, Boeretang 200, 2400, Mol, Belgium) ,  Van Renterghem W. (SCK・CEN, Nuclear Materials Science Institute, Boeretang 200, 2400, Mol, Belgium) ,  Van den Berghe S. (SCK・CEN, Nuclear Materials Science Institute, Boeretang 200, 2400, Mol, Belgium) ,  Detavernier C. (Ghent University, Department of Solid State Sciences, Krijgslaan 281/S1, 9000, Ghent, Belgium) ,  Evans J.H. (School of Computing and Engineering, University of Huddersfield, Huddersfield, HD1 3DH, UK)
資料名： Journal of Nuclear Materials  (Journal of Nuclear Materials)
巻： 529  ページ： Null  発行年： 2020年 
JST資料番号： D0148A  ISSN： 0022-3115  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 10%,15%,20%および25%~235U燃焼度を有するU7wt%Moの低燃焼度サンプルを,核分裂ガスナノバブル格子の形成機構を研究するために,透過型電子顕微鏡によって分析した。解析によると,気泡格子形成は10%以下の燃焼度で始まり,照射線量の増加と共に粒内部に広がる前に粒界に優先的に形成された。気泡格子の幾何学的特性と秩序化の程度は燃料の核分裂密度に無関係であると思われる。圧力計算は,解析した4つの試料において気泡が極端に加圧されていることを示し,従って,それらの配列の最初の段階における空洞のボイド状の性質を示唆している。最後に,気泡格子破壊の最初の兆候は,燃料再結晶による20%の燃焼度に近づくと,結晶粒界で観察される。提示した結果は,照射したU(Mo)における核分裂ガスナノバブル格子の開発へのさらなる洞察を提供する。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 気泡 ,  金属燃料 ,  核分裂 ,  核燃料燃焼度 ,  *中性子照射 ,  核分裂気体 ,  透過型電子顕微鏡 ,  電子顕微鏡観察 ,  照射線量 ,  結晶粒界 ,  格子形成 ,  再結晶 ,  *ウルトラファインバブル ,  度
準シソーラス用語： 形成機構 ,  *ナノバブル , 【Automatic Indexing@JST】

著者キーワード (6件)： 金属燃料 ,  UMO ,  低燃焼度 ,  透過型電子顕微鏡 ,  ナノバブル格子 ,  核分裂ガス

分類 (1件)： 核燃料の基礎的性質  (MD08020V)