ナノスケール結晶内細孔を有する軽量アルミナの作製【JST・京大機械翻訳】

Fabrication of lightweight alumina with nanoscale intracrystalline pores

著者 (5件)： Fu Lvping (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China) ,  Gu Huazhi (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China) ,  Huang Ao (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China) ,  Zou Yongshun (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China) ,  Zhang Meijie (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, China)
資料名： Journal of the American Ceramic Society  (Journal of the American Ceramic Society)
巻： 103  号： 3  ページ： 2262-2271  発行年： 2020年 
JST資料番号： C0253A  ISSN： 0002-7820  CODEN： JACTAW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,ジルコニアゾルとアルミナゾルをα-Al_2O_3微粉末に導入することにより,ナノスケールの結晶内細孔を含む軽量アルミナを作製した。軽量アルミナの焼結挙動に及ぼすジルコニアゾルの影響も調べた。ジルコニアゾルの導入により,ナノ-アルミナの粒成長と相変態は遅れた。従って,ナノ粒子間のナノスケール細孔の構造は熱処理中に安定化され,50~300nmの範囲の直径を持つ多数のナノスケール結晶内細孔がアルミナ粒子中に捕捉された。これらのナノスケール結晶内細孔の存在のため,軽量アルミナの熱伝導率は著しく減少した。0.75wt%ジルコニアゾルの添加による軽量アルミナはジルコニアゾルなしのアルミナと比較して31%低い熱伝導率を示した。Copyright 2020 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 細孔 ,  ナノ粒子 ,  微粉体 ,  *結晶 ,  熱伝導率 ,  結晶成長 ,  熱処理 ,  *アルミナ ,  焼結
準シソーラス用語： アルミナ粒子 ,  アルミナゾル ,  軽量 ,  *ナノスケール , 【Automatic Indexing@JST】

著者キーワード (4件)： 粒成長 ,  軽量アルミナ ,  ナノスケールの結晶内細孔 ,  焼結挙動

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (6件)： ナノスケール ,  結晶 ,  細孔 ,  軽量 ,  アルミナ ,  作製