Carbon nanotube-based mixed-matrix membranes with supramolecularly engineered interface for enhanced gas separation performance

著者 (5件)： Zhang Qinnan (Department of Chemical and Biomolecular Engineering, University of Notre Dame, Notre Dame, IN, 46556, United States) ,  Li Si (Department of Chemical and Biomolecular Engineering, University of Notre Dame, Notre Dame, IN, 46556, United States) ,  Wang Ceming (Department of Chemical and Biomolecular Engineering, University of Notre Dame, Notre Dame, IN, 46556, United States) ,  Chang Hsueh-Chia (Department of Chemical and Biomolecular Engineering, University of Notre Dame, Notre Dame, IN, 46556, United States) ,  Guo Ruilan (Department of Chemical and Biomolecular Engineering, University of Notre Dame, Notre Dame, IN, 46556, United States)
資料名： Journal of Membrane Science  (Journal of Membrane Science)
巻： 598  ページ： Null  発行年： 2020年 
JST資料番号： E0669A  ISSN： 0376-7388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,新しいナノ複合膜を単層カーボンナノチューブ(SWNTs)とトリプチセン含有ポリイミドから作製した。SWNTの望ましい界面形態と均一な分散は,高分子マトリックス中のナノチューブとパドル状トリプチセン部分の間の強いπ-πスタッキングと超分子形状適合相互作用によって達成された。購入したままのSWNT(AP-SWNT)の2~15wt%を含む混合マトリックス膜(MMMs)を調製し,それらのガス輸送特性を試験した。全てのMMMsは良く維持された選択性で透過性を大きく増強したが,充填剤含有量に対する透過率の非線形依存性が観察された。精製したSWNT(p-SWNTs)と酸処理SWNT(A-SWNT)を有する他の一連のMMMsも調製した。官能化A-SWNT MMMは,すべてのMMMsの中で2wt%充填剤含有量で最良の分離性能を示し,これはA-SWNTsのカルボン酸官能化表面との界面親和性の改善に起因した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *カーボンナノチューブ ,  ポリイミド ,  透過率 ,  相互作用 ,  カルボン酸 ,  親和性 ,  *ナノチューブ ,  ガス分離 ,  酸処理 ,  *界面 ,  *超分子 ,  官能化 ,  単層カーボンナノチューブ
準シソーラス用語： *分離性能 ,  ナノ複合膜 , 【Automatic Indexing@JST】

著者キーワード (4件)： 混合マトリックス膜 ,  トリプチセン含有ポリイミド ,  単層カーボンナノチューブ ,  ガス分離

分類 (1件)： 膜分離  (XD02120Z)

タイトルに関連する用語 (6件)： 増強 ,  ガス分離性能 ,  分子工学 ,  界面 ,  カーボンナノチューブ ,  混合マトリックス膜