プラズマ酸化処理したTi6Al4V合金のトライボロジー特性に及ぼす温度の影響【JST・京大機械翻訳】

The Influence of Temperature on the Tribological Properties of the Ti₆Al₄V Alloy Treated by Plasma Oxidation

著者 (5件)： Siqueira Rafael Coelho (Federal University of Sao Carlos - UFSCar, Sorocaba Brazil Sao Paulo Rodovia Joao Leme dos Santos, Km 110, Bairro do Itinga) ,  de Almeida Larissa Solano (Federal University of Sao Carlos - UFSCar, Sorocaba Brazil Sao Paulo Rodovia Joao Leme dos Santos, Km 110, Bairro do Itinga) ,  Manfrinato Marcos Dorigao (Sorocaba Technological College - FATEC, Sorocaba Brazil Av. Engenheiro Carlos Reinaldo Mendes, 2015) ,  Moreto Jeferson Aparecido (Federal University of Triangulo Mineiro (UFTM), Institute of Exact Sciences, Naturals and Education Uberaba Brazil Avenida Doutor Randolfo Borges Junior, Univerdecidade) ,  Rossino Luciana Sgarbi (Federal University of Sao Carlos - UFSCar, Sorocaba Brazil Sao Paulo Rodovia Joao Leme dos Santos, Km 110, Bairro do Itinga)
資料名： Materials Science Forum  (Materials Science Forum)
巻： 1012  ページ： 418-423  発行年： 2020年 
JST資料番号： D0716B  ISSN： 0255-5476  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： プラズマ酸化プロセスの目的は,材料中の天然酸化物を厚くすることによって,Ti6Al4V合金の硬度,耐食性,および生体適合性を向上させることである。本研究の目的は,プラズマ酸化処理したTi6Al4V合金の厚さ,硬度および耐摩耗性に及ぼす温度の影響を検証することである。パルスDC真空反応器を用いて,480°C,520°C,670°Cおよび705°Cの温度で,1時間の処理に対して,60%Arおよび40%O_2および1.65torr圧力のガス比で,処理を行なった。アナターゼとルチルの多層形成に関しては,処理温度の上昇と共に層厚が増加することが観察された。処理による表面硬度の増加は,研究した材料の耐摩耗性をかなり増加させた。最大層厚と表面硬度は705°Cで処理した材料で得られたが,最低摩耗体積は520°Cで処理した材料で得られた。Copyright 2020 Trans Tech Publications Ltd. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 耐摩耗性 ,  *摩耗 ,  酸化物 ,  耐食性 ,  反応器 ,  ルチル ,  パルス ,  層厚 ,  硬度 ,  アブレシブ摩耗 ,  アナターゼ ,  生体適合性
準シソーラス用語： *プラズマ酸化 ,  *トライボロジー特性 ,  表面硬度 , 【Automatic Indexing@JST】

著者キーワード (4件)： アナターゼ ,  ルチル ,  プラズマ酸化 ,  マイクロアブレシブ摩耗

分類 (2件)： 機械的性質  (WB02030U) ,  表面硬化熱処理  (WC03030E)

タイトルに関連する用語 (2件)： プラズマ酸化 ,  トライボロジー特性