ニッケル基合金GH3039のガスタングステンアーク溶接中の柱状結晶粒進展のマクロ-ミクロスケールモデリングとシミュレーション【JST・京大機械翻訳】

Macro-Micro Scale Modeling and Simulation of Columnar Grain Evolution During Gas Tungsten Arc Welding of Nickel-Based Alloy GH3039

著者 (4件)： Chen Lili (College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, P.R. China) ,  Wei Yanhong (College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, P.R. China) ,  Qiu Shufan (College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, P.R. China) ,  Zhao Wenyong (College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing, P.R. China)
資料名： Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science  (Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science)
巻： 51  号： 2  ページ： 887-896  発行年： 2020年 
JST資料番号： E0265B  ISSN： 1073-5623  CODEN： MTTABN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： ガスタングステンアーク溶接で得られたニッケル基合金GH3039溶融池の凝固微細構造をシミュレートするために,有限要素法と組み合わせたセルラオートマトンモデルを開発した。有限要素モデルでシミュレートしたマクロ温度場をセルラオートマトン格子に投影した。メッシュに基づいて,溶融池におけるエピタキシャル核形成と競合成長を行った。凝固進展に及ぼす母材粒組織と溶接条件の影響を研究した。その結果,柱状結晶粒の幅は初期結晶粒サイズが成長すると増加することが分かった。溶融池の形状と熱分布は溶接条件によって変化する。競合成長は温度勾配方向により支配的であり,溶接部の結晶粒構造は最終的には融合線に垂直になる傾向があった。実験継手の形状と微細構造を光学顕微鏡と電子後方散乱回折を用いて完全に特性化した。シミュレーション結果は,対応する実験結果と良く一致し,電流モデルの精度を検証した。Copyright 2019 The Minerals, Metals & Materials Society and ASM International Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 溶接条件 ,  *TIG溶接 ,  電流 ,  *結晶粒 ,  エピタクシー ,  凝固 ,  セルラオートマトン ,  *ニッケル合金 ,  *柱状晶 ,  温度勾配 ,  結晶粒径 ,  有限要素法 ,  溶接部 ,  *シミュレーション ,  溶融池