銅における二重衝撃誘起スポールおよび再圧縮過程【JST・京大機械翻訳】

Double-shock-induced spall and recompression processes in copper

著者 (5件)： Wang JiaNan (CAS Key Laboratory of Mechanical Behavior and Design of Materials, Department of Modern Mechanics, University of Science and Technology of China, Hefei, Anhui 230027, China) ,  Wu FengChao (CAS Key Laboratory of Mechanical Behavior and Design of Materials, Department of Modern Mechanics, University of Science and Technology of China, Hefei, Anhui 230027, China) ,  Wang Pei (Institute of Applied Physics and Computational Mathematics, Beijing 100094, China) ,  He AnMin (Institute of Applied Physics and Computational Mathematics, Beijing 100094, China) ,  Wu HengAn (CAS Key Laboratory of Mechanical Behavior and Design of Materials, Department of Modern Mechanics, University of Science and Technology of China, Hefei, Anhui 230027, China)
資料名： Journal of Applied Physics  (Journal of Applied Physics)
巻： 127  号： 13  ページ： 135903-135903-9  発行年： 2020年 
JST資料番号： C0266A  ISSN： 0021-8979  CODEN： JAPIAU  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 多重衝撃波によって引き起こされる破砕損傷は,重要で重要な課題である。ここでは,二重衝撃負荷銅における衝撃損傷と再圧縮過程を調べるために分子動力学シミュレーションを行った。従来の全信号と比較して,ピーク間の異なる時間間隔を有する2つの有意な速度ピークが,2つの衝撃負荷の下で自由表面速度において観察された。次に,動的過程をボイドの進展と波動の複雑な伝搬を通して明らかにした。一方,衝撃荷重後の回復試料の状態は荷重条件に依存することが分かった。再圧縮を受ける完全な試料と分離された破砕片を持つ壊れた試料の両方を著者らのシミュレーションで観察した。二次破砕は再圧縮プロセス後に観察され,関連する破砕強度は最初の衝撃荷重下のそれより著しく低い。再結晶は,高度に局所化された塑性変形の残留物による二次衝撃荷重後の破砕領域で観察された。シミュレーション結果を温度-圧力経路により得られた試料の熱力学的性質に基づいて確認した。Copyright 2020 AIP Publishing LLC All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *銅 ,  *衝撃 ,  塑性変形 ,  衝撃荷重 ,  自由表面 ,  再結晶 ,  計算機シミュレーション ,  熱力学的性質 ,  シミュレーション ,  多重化 ,  波動 ,  衝撃波
準シソーラス用語： 局在化 ,  荷重条件 ,  分子動力学シミュレーション ,  衝撃損傷 , 【Automatic Indexing@JST】