ルブレン高分子複合体膜の一重項励起子分裂に及ぼす銀ナノプレート効果

Effect of silver nanoplate on singlet exciton fission in rubrene polymer-composite films

著者 (5件)： Yonemura Hiroaki (Department of Nanoscience, Faculty of Engineering, Sojo University, 4-22-1 Ikeda, Nishi-ku, Kumamoto 860-0082, Japan) ,  Aira Daiki (Department of Nanoscience, Faculty of Engineering, Sojo University, 4-22-1 Ikeda, Nishi-ku, Kumamoto 860-0082, Japan) ,  Asakura Nanami (Department of Nanoscience, Faculty of Engineering, Sojo University, 4-22-1 Ikeda, Nishi-ku, Kumamoto 860-0082, Japan) ,  Ezoe Kosumo (Department of Nanoscience, Faculty of Engineering, Sojo University, 4-22-1 Ikeda, Nishi-ku, Kumamoto 860-0082, Japan) ,  Sakaguchi Hiroshi (Institute of Advanced Energy, Kyoto University, Gokasho, Uji, Kyoto 611-0011, Japan)
資料名： Japanese Journal of Applied Physics  (Japanese Journal of Applied Physics)
巻： 59  号： SD  ページ： SDDB03 (7pp)  発行年： 2020年03月 
JST資料番号： G0520B  ISSN： 0021-4922  CODEN： JJAPB6  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： AgPL有無における2つのRub高分子複合体厚膜のRubの蛍光強度磁場依存性の測定を通じて,RubのSFに及ぼす磁場効果(MFEs)を調べることにより,ルブレン(Rub)の一重項励起子分裂(SF)に及ぼす銀ナノプレート(AgPL)効果を実証した。Rub-AgPL高分子複合膜のRub蛍光強度は,Rub高分子複合体膜のそれより大きかった。増強(1.4倍)は,高分子マトリクス中のRub近くに埋め込まれたAgPLの局在表面プラズモン共鳴(LSPR)による強い電場が原因に違いない。Rub-AgPL高分子複合膜のMFEsの大きさは,Rub高分子複合体膜におけるそれらとほとんど同じであった。これらの結果から,SF効率が,Rub-AgPL高分子複合体膜中でポリマーマトリクスへの埋込みAgPLによるLSPRによって増強されることを強く示す。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.

シソーラス用語： *芳香族縮合炭化水素 ,  *ポリメタクリル酸メチル ,  *高分子複合体 ,  高分子膜 ,  厚膜 ,  *銀 ,  *ナノ構造 ,  *蛍光 ,  *磁場効果 ,  エネルギー移動 ,  *励起子 ,  *プラズマ共鳴 ,  埋込み【挿入】 ,  局在表面プラズモン共鳴
準シソーラス用語： ナノプレート ,  一重項分裂

分類 (1件)： 有機化合物のルミネセンス  (BM08094A)

物質索引 (1件)： ルブレン

タイトルに関連する用語 (6件)： ルブレン ,  高分子複合体 ,  一重項 ,  励起子 ,  銀 ,  ナノプレート