溶融フッ化物塩中における316Lステンレス鋼と黒鉛のガルバニック腐食【JST・京大機械翻訳】

Galvanic corrosion of Type 316L stainless steel and Graphite in molten fluoride salt

著者 (6件)： Qiu Jie (Department of Nuclear Engineering, University of California at Berkeley, Berkeley, CA 94720, USA) ,  Wu Angjian (Department of Nuclear Engineering, University of California at Berkeley, Berkeley, CA 94720, USA) ,  Li Yanhui (Department of Nuclear Engineering, University of California at Berkeley, Berkeley, CA 94720, USA) ,  Xu Yi (Department of Nuclear Engineering, University of California at Berkeley, Berkeley, CA 94720, USA) ,  Scarlat Raluca (Department of Nuclear Engineering, University of California at Berkeley, Berkeley, CA 94720, USA) ,  Macdonald Digby D. (Department of Nuclear Engineering, University of California at Berkeley, Berkeley, CA 94720, USA)
資料名： Corrosion Science  (Corrosion Science)
巻： 170  ページ： Null  発行年： 2020年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： タイプ316Lステンレス鋼(SS)の腐食に及ぼすグラファイトの影響を,電気化学的方法を用いて,溶融FLiNaK(LiF-NaF-KF:46.5~11.5~42mol%)塩中で研究した。結果は,Ohm的に結合したとき,タイプ316L SSとGraphiteが溶融フッ化物塩におけるガルバニック腐食に敏感であることを示した。より正の起電力を持つGraphiteは,タイプ316L SS/Graphiteガルバニック対におけるカソードとして作用し,鋼の腐食を加速する。溶融FLiNaK塩におけるタイプ316L SSに及ぼすGraphiteのガルバニ効果は,グラファイト/タイプ316L SS表面積比,温度,および塩の水分不純物の増加とともに直線的に増加した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 起電力 ,  表面積 ,  不純物 ,  *腐食 ,  *鋼 ,  *グラファイト ,  融解塩 ,  フッ化ナトリウム ,  *フッ化物 ,  水分 ,  電気化学 ,  *電池作用腐食 ,  カソード
準シソーラス用語： *SUS316L , 【Automatic Indexing@JST】

著者キーワード (5件)： 溶融塩 ,  Flinak ,  316Lステンレス鋼 ,  グラファイト ,  腐食

分類 (1件)： 腐食  (WB03030B)