EK61超合金の長時間時効中の破壊形態と微細組織変化の間の相関【JST・京大機械翻訳】

Correlation between Fracture Morphology and Microstructural Evolution during Long-Term Aging of EK61 Superalloy

著者 (5件)： Huang Jin (School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China) ,  Huang Jin (High-Temperature Materials Department, China Iron & Steel Research Institute Group, Beijing 100081, China) ,  Xu Guohua (High-Temperature Materials Department, China Iron & Steel Research Institute Group, Beijing 100081, China) ,  Qin Heyong (High-Temperature Materials Department, China Iron & Steel Research Institute Group, Beijing 100081, China) ,  Zheng Lei (School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China)
資料名： Scanning  (Scanning)
巻： 2020  ページ： Null  発行年： 2020年 
JST資料番号： D0300B  ISSN： 0161-0457  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 700°Cと750°Cで1000hまでの長期時効中のEK61超合金のミクロ組織変化を,走査Electron顕微鏡(SEM)と透過Electron顕微鏡(TEM)の組合せによって研究した。SEMにより異なる時間時効後の衝撃破壊形態を観察した。ミクロ組織は700°Cでの時効中に比較的安定であり,破壊形態は粒内破壊によって特徴付けられた。750°Cでは,γ[数式:原文を参照]相の粗大化はディンプルの量の減少をもたらし,粒界上の炭化物の連鎖化は粒界破壊をもたらし,結晶粒内のη相のネットティングはラメラ劈開段階の形成をもたらす。析出相の不安定化が破壊形態に大きく影響することは明白である。破壊形態と微細構造の間の関係は,EK61超合金のサービス信頼性の評価を促進する。Copyright 2020 Jin Huang et al. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 結晶粒界 ,  *時効 ,  微細構造 ,  信頼性 ,  炭化物 ,  *超合金 ,  結晶粒 ,  粒内破壊 ,  粒界破壊 ,  η相
準シソーラス用語： ディンプル ,  不安定化 ,  衝撃破壊 ,  微細構造進展 ,  破壊形態 , 【Automatic Indexing@JST】

分類 (3件)： 生体の顕微鏡観察法  (EA03050C) ,  顕微鏡法  (BK01040E) ,  固体デバイス製造技術一般  (NC03030V)

引用文献 (20件)：

• A. M. Polyanskii, V. M. Polyanskii, "Structural changes in alloy ÉK61 due to cyclic deformation at elevated temperature," Metal Science and Heat Treatment, vol. 52, no. 5-6, pp. 279-283, 2010.
• V. N. Semenov, N. V. Akimov, V. P. Glushko, "Formation of cracks in EP202 and EK61 alloys in welding of structures of liquid rocket engines," Welding International, vol. 27, no. 2, pp. 159-162, 2013.
• K. I. Nedashkovskii, O. N. Zheleznyak, B. M. Gromyko, B. A. Kozykov, I. A. Mikhalev, "Effect of low temperatures on mechanical and physical properties of high-strength nickel alloy ÉK61ID and stainless maraging steel ÉK49VD," Metal Science and Heat Treatment, vol. 45, no. 5-6, pp. 233-236, 2003.
• E. Galieva, V. Valitov, R. Lutfullin, A. Bikmukhametova, "Low-temperature superplasticity of the Ni-based EK61 superalloy and application of this effect to obtain Sound solid phase joints," Defect and Diffusion Forum, vol. 385, pp. 150-154, 2018.
• M. Jouiad, E. Marin, R. S. Devarapalli, J. Cormier, F. Ravaux, C. Le Gall, J.-M. Franchet, "Microstructure and mechanical properties evolutions of alloy 718 during isothermal and thermal cycling over-aging," Materials and Design, vol. 102, pp. 284-296, 2016.

タイトルに関連する用語 (6件)： 超合金 ,  長時間 ,  時効 ,  破壊形態 ,  微細組織 ,  相関