レーザ表面再溶融Al-Cu合金における結晶粒微細化の理解【JST・京大機械翻訳】

Understanding the refinement of grains in laser surface remelted Al-Cu alloys

著者 (7件)： Patel M.N. (Centre for Additive Manufacturing, School of Engineering, RMIT University, Melbourne, Victoria, Australia) ,  Qiu D. (Centre for Additive Manufacturing, School of Engineering, RMIT University, Melbourne, Victoria, Australia) ,  Wang G. (Centre for Advanced Materials Processing and Manufacturing, School of Mechanical and Mining Engineering, University of Queensland, Queensland, Australia) ,  Gibson M.A. (CSIRO Manufacturing, Clayton, Victoria, Australia) ,  Prasad A. (Centre for Advanced Materials Processing and Manufacturing, School of Mechanical and Mining Engineering, University of Queensland, Queensland, Australia) ,  StJohn D.H. (Centre for Advanced Materials Processing and Manufacturing, School of Mechanical and Mining Engineering, University of Queensland, Queensland, Australia) ,  Easton M.A. (Centre for Additive Manufacturing, School of Engineering, RMIT University, Melbourne, Victoria, Australia)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 178  ページ： 447-451  発行年： 2020年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： レーザ表面再溶融(LSR)Al-xwt.%Cu(x=2,5&7)の粗粒微細構造はAl-3Ti-1B結晶粒微細化剤により著しく微細化された。溶融池境界でのエピタキシャル柱状粒成長は抑制された。約80%の結晶粒サイズの減少が達成され,添加したTiB_2粒子の25%以上が,鋳造中に活性化された0.1%未満と比較して活性化されるように見えた。核形成速度の増加は,熱過冷却の増加,より低いポテンシャルの多数の核生成物の活性化,および核形成自由ゾーンのサイズの減少によって説明される。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  エピタクシー ,  *結晶粒微細化 ,  柱状晶 ,  溶融池 ,  急冷凝固 ,  過冷却 ,  核形成 ,  凝固 ,  鋳造 ,  結晶粒径 ,  *レーザ ,  アルミニウム合金 ,  微細構造 ,  精密化

著者キーワード (5件)： アルミニウム合金 ,  結晶粒微細化 ,  急冷凝固 ,  凝固微細構造 ,  核形成自由領域