二次元水酸化ニッケルから直接の強磁性金属転換【JST・京大機械翻訳】

Ferromagnetic metal conversion directly from two-dimensional nickel hydroxide

著者 (7件)： Naruo Yuhsuke (Graduate School of Science and Technology, Kumamoto University, Kumamoto 860-8555, Japan) ,  Uechi Seita (Graduate School of Science and Technology, Kumamoto University, Kumamoto 860-8555, Japan) ,  Sawada Masahiro (Hiroshima Synchrotron Radiation Center, Hiroshima University, Hiroshima 739-0046, Japan) ,  Funatsu Asami (Faculty of Advanced Science and Technology, Kumamoto University, Kumamoto 860-8555, Japan) ,  Shimojo Fuyuki (Faculty of Advanced Science and Technology, Kumamoto University, Kumamoto 860-8555, Japan) ,  Ida Shintaro (Faculty of Advanced Science and Technology, Kumamoto University, Kumamoto 860-8555, Japan) ,  Hara Masahiro (Faculty of Advanced Science and Technology, Kumamoto University, Kumamoto 860-8555, Japan)
資料名： Nanotechnology  (Nanotechnology)
巻： 31  号： 43  ページ： 435602 (5pp)  発行年： 2020年 
JST資料番号： W0108A  ISSN： 0957-4484  CODEN： NNOTER  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 真空中での熱アニーリングにより,水酸化ニッケルナノシートからニッケル金属ナノ構造への直接金属変換を実証した。Si基板上に析出した単層ナノシートの金属転移をX線吸収端近傍構造(XANES)測定により明らかにした。XANES信号は,250°C以上のアニーリング温度で著しく変化した。金属転移温度は,層状水酸化ニッケルナノシートが空気中でのか焼によって酸化ニッケルナノシートに変換する報告温度と一致する。Auger測定は,水酸化物ナノシートからの酸素の解離が金属変換を誘起することを確認した。変換ニッケル金属構造は,X線磁気円二色性(XMCD)測定によって明らかにされた強磁性挙動を示した。原子間力顕微鏡測定は,基板上へのニッケル原子の拡散が2D様構造から粒子様構造への構造変化をもたらすことを示した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *強磁性 ,  転移温度 ,  酸素 ,  *ニッケル ,  *酸化ニッケル ,  水酸化物 ,  か焼 ,  *二次元 ,  XANES ,  原子間力顕微鏡 ,  ナノシート
準シソーラス用語： アニーリング温度 ,  *水酸化ニッケル ,  構造変化 ,  熱アニーリング , 【Automatic Indexing@JST】