WC-Co超硬合金の固体粒子エロージョン摩耗抵抗の研究【JST・京大機械翻訳】

Study of Solid Particle Erosion Wear Resistance of WC-Co Cemented Carbide

著者 (7件)： Feng Chunyu (Key Laboratory of Oil and Natural Gas Equipment, Ministry of Education, Chengdu, People’s Republic of China) ,  Feng Chunyu (School Mechatronic Engineering, Southwest Petroleum University, Chengdu, People’s Republic of China) ,  Chen Du (School Mechatronic Engineering, Southwest Petroleum University, Chengdu, People’s Republic of China) ,  Xu Mingjun (PetroChina Tarim Oilfield Company, Korla, People’s Republic of China) ,  Shen Cong (PetroChina Tarim Oilfield Company, Korla, People’s Republic of China) ,  Yang Lei (PetroChina Tarim Oilfield Company, Korla, People’s Republic of China) ,  Jiang Jiwei (Chongqing Chuanyi Control Valve Limited Company, Chongqing, People’s Republic of China)
資料名： Journal of Failure Analysis and Prevention  (Journal of Failure Analysis and Prevention)
巻： 20  号： 2  ページ： 543-554  発行年： 2020年 
JST資料番号： W4576A  ISSN： 1547-7029  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本論文では,WC-Co超硬合金のエロージョン摩耗に影響するいくつかの主要因子を試験し,超硬合金固体粒子エロージョン試験により解析した。エロージョン角に加えて,ターゲット材料に影響を与えた後の研磨剤の衝撃速度,硬度および寸法,および研磨剤の破壊の程度も,エロージョン摩耗結果に及ぼす著しい影響を有した。エロージョン後の高い破砕度を持つ研磨剤は超硬合金のエロージョン摩耗効率が低い。Co含有量とWC粒径の増加は超硬合金のエロージョン抵抗の低下をもたらす。エロージョン後のターゲット材料のエネルギースペクトル解析の後,Co粒子が最初にエロージョン過程で分離されることが分かった。その後,全体の微細構造の不安定性のために,一連の浸食摩耗が引き起こされた。Copyright ASM International 2020 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 浸食 ,  *耐摩耗性 ,  微細構造 ,  *摩耗 ,  *超硬合金 ,  耐食性 ,  粒径 ,  スペクトル解析 ,  研磨剤 ,  不安定性 ,  硬度
準シソーラス用語： *エロージョン ,  衝撃速度 ,  *固体粒子エロージョン ,  *エロージョン摩耗 , 【Automatic Indexing@JST】

著者キーワード (4件)： WC-Co ,  超硬合金 ,  耐食性 ,  エロージョン機構

分類 (1件)： 潤滑一般  (QB02010S)

タイトルに関連する用語 (5件)： WC-Co ,  超硬合金 ,  固体粒子エロージョン ,  摩耗抵抗 ,  研究