膜蒸留における超薄高密度親水性層レジスト濡れを有する複合Janus膜【JST・京大機械翻訳】

Can Composite Janus Membranes with an Ultrathin Dense Hydrophilic Layer Resist Wetting in Membrane Distillation?

著者 (5件)： Chen Yuanmiaoliang (NUS Graduate School for Integrative Science and Engineering, National University of Singapore, Singapore) ,  Lu Kang-Jia (Department of Chemical and Biomolecular Engineering, National University of Singapore, Singapore) ,  Japip Susilo (Department of Chemical and Biomolecular Engineering, National University of Singapore, Singapore) ,  Chung Tai-Shung (NUS Graduate School for Integrative Science and Engineering, National University of Singapore, Singapore) ,  Chung Tai-Shung (Department of Chemical and Biomolecular Engineering, National University of Singapore, Singapore)
資料名： Environmental Science & Technology  (Environmental Science & Technology)
巻： 54  号： 19  ページ： 12713-12722  発行年： 2020年 
JST資料番号： B0839A  ISSN： 0013-936X  CODEN： ESTHA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 膜湿潤は,膜蒸留(MD)の大規模応用に対する進行中の課題である。ここでは,超薄緻密親水性層から成る複合Janus MD膜を,疎水性ポリフッ化ビニリデン基板上にカチオン性ポリエチレンイミンおよびアニオン性ポリ-(ナトリウム4-スチレンスルホナート高分子電解質を積層することにより開発した。低表面張力の供給物として界面活性剤含有塩水を用いて,実験は,表面濡れ性または表面電荷よりむしろ高分子電解質層の数が,複合Janus膜の耐濡れ性能を決定することを明らかにした。より多くの堆積層はより高い濡れ抵抗をもたらした。陽電子消滅分光法の助けにより,この研究は,初めて,複合材料Janus膜の優れたぬれ抵抗の起源を示した。高分子電解質多層の有効孔径は堆積層数の増加と共に減少する。48nmの超薄親水性多層を有する膜は,サイズ排除機構を介して供給溶液から界面活性剤分子をふるいにふるいに十分に小さな細孔径を持ち,従って,疎水性基板を低表面張力供給水によって濡れることから保護する。本研究は,堅牢な膜蒸留のための次世代抗湿潤Janus膜を開発する道を開いた。Copyright 2020 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面張力 ,  *濡れ ,  界面活性剤 ,  高分子電解質 ,  *親水性 ,  疎水性 ,  ポリエチレンイミン ,  湿潤 ,  ポリフッ化ビニリデン ,  カチオン ,  *レジスト ,  表面電荷 ,  多層 ,  ロバスト性
準シソーラス用語： 表面濡れ性 , 【Automatic Indexing@JST】