Al-7075合金の付加製造のためのアルミニウム粉末の表面接種【JST・京大機械翻訳】

Surface inoculation of aluminium powders for additive manufacturing of Al-7075 alloys

著者 (8件)： Vieth P. (Paderborn University, Technical and Macromolecular Chemistry, Paderborn) ,  Voigt M. (Paderborn University, Technical and Macromolecular Chemistry, Paderborn) ,  Ebbert C. (Paderborn University, Technical and Macromolecular Chemistry, Paderborn) ,  Milkereit B. (University of Rostock, Materials Technology and Competence Center °Calor, Rostock) ,  Zhuravlev E. (University of Rostock, Materials Technology and Competence Center °Calor, Rostock) ,  Yang B. (University of Rostock, Materials Technology and Competence Center °Calor, Rostock) ,  Kessler O. (University of Rostock, Materials Technology and Competence Center °Calor, Rostock) ,  Grundmeier G. (Paderborn University, Technical and Macromolecular Chemistry, Paderborn)
資料名： Procedia CIRP  (Procedia CIRP)
巻： 94  ページ： 17-20  発行年： 2020年 
JST資料番号： W3527A  ISSN： 2212-8271  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： レーザー粉末層融合(LPBF)では,特にレーザ融解プロセス後の凝固中に,高エネルギー入力が材料中の細孔や亀裂のような欠陥を引き起こすので,高強度アルミニウム材料(Al-7075のような)の生成が特別な課題である。この問題を克服するために,ナノ粒子をL-PBFプロセスに用いた粉末の表面上に吸着した。この添加は,結晶粒微細化と製造プロセス中の熱間亀裂形成の低減を目的とする。この寄与は,TiCナノ粒子によるアルミニウム粒子の表面接種のプロセス,並びに,示差高速走査熱量測定(DFSC)による融解と凝固温度の測定を示す。DFSCの助けにより,改良凝固プロセスが観察された。従って,ナノ粒子はアルミニウム粉末の急速凝固中に核形成障壁を改善した核として作用する。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 核形成 ,  凝固 ,  亀裂 ,  *合金 ,  *粉体 ,  熱量測定 ,  *アルミニウム ,  高温割れ ,  結晶粒微細化 ,  凝固点 ,  生産工程 ,  急冷凝固 ,  レーザ融解 ,  ナノ粒子 ,  *付加製造

著者キーワード (5件)： AA7075 ,  表面接種 ,  L-PBF ,  DFSC ,  ナノ粒子

分類 (4件)： 圧粉,焼結  (WC02030X) ,  レーザの応用  (BD04100V) ,  鋳造に関する各種技術  (WC01040B) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： Al ,  付加製造 ,  アルミニウム粉末 ,  接種