Mgにおける脱双晶媒介硬化:単一双晶境界の微小圧縮研究【JST・京大機械翻訳】

Detwinning-mediated hardening in Mg: A microcompression study of a single twin boundary

著者 (4件)： Maghsoudi Mohammadhadi (Helmholtz-Zentrum Geesthacht, Institute of Materials Research, Materials Mechanics, 21502, Geesthacht, Germany) ,  Ziehmer Markus (Helmholtz-Zentrum Geesthacht, Institute of Materials Research, Materials Mechanics, 21502, Geesthacht, Germany) ,  Lilleodden Erica T. (Helmholtz-Zentrum Geesthacht, Institute of Materials Research, Materials Mechanics, 21502, Geesthacht, Germany) ,  Lilleodden Erica T. (Hamburg University of Technology, Institute of Advanced Ceramics, 21073, Hamburg, Germany)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 772  ページ： Null  発行年： 2020年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Mg中の単一双晶境界の脱双晶から生じる硬化の最初の実験的測定を示した。マイクロ圧縮試験を2セットのマイクロカラムで行った。(i)圧縮軸に沿ってほぼ(0001)の「親」結晶方位を持つ単結晶,(ii)母結晶粒と単一{1012}双晶境界を含む双結晶。応力-ひずみデータの比較により,変形マイクロカラムの変形特性に有意差があることを示した。双結晶マイクロカラムは,応力プラトーによって示されるように,脱双晶を起こし,それは母結晶粒の配向の公称単結晶マイクロカラムをもたらす。プラトーを超えた微小圧縮は,脱双晶マイクロカラムが単結晶「親」マイクロカラムよりもかなり高い降伏応力と歪硬化速度を示すことを示した。変形マイクロカラムの断面に関するElectron後方散乱回折解析は,変形した母マイクロカラムと比較して,非対転位(いわゆるGNDs)の高い含有量を示す脱双晶領域におけるより高いミスオリエンテーションを明らかにした。試料間の方位差分布におけるこの矛盾は,観察されたように,双晶化による硬化応答と一致し,脱双晶過程の結果としての転位デブリの生成を示す。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 単結晶 ,  *マグネシウム ,  歪硬化 ,  圧縮試験 ,  後方散乱 ,  結晶方位 ,  双結晶 ,  加工硬化 ,  *双晶境界 ,  微視力学 ,  結晶粒 ,  降伏応力 ,  回折 ,  *双晶
準シソーラス用語： 双晶化 , 【Automatic Indexing@JST】

著者キーワード (4件)： マイクロメカニクス ,  マグネシウム ,  双晶 ,  加工硬化

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)