層状複合粉末によるミクロ組織最適化Fe-Cu-Ni-P焼結合金における強度-塑性衝突の回避【JST・京大機械翻訳】

Evading strength-plasticity conflict in microstructure-optimized Fe-Cu-Ni-P sintered alloy via layered-composite powder

著者 (7件)： Jiang Runjian (School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, China) ,  Jiang Runjian (Powder Technology Laboratory, San Diego State University, San Diego, USA) ,  Cui Guodong (School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, China) ,  Olevsky Eugene A. (Powder Technology Laboratory, San Diego State University, San Diego, USA) ,  Olevsky Eugene A. (NanoEngineering, University of California, San Diego, La Jolla, USA) ,  Zhang Chengsong (School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, China) ,  Chen Dazhi (School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, China)
資料名： Materialia  (Materialia)
巻： 14  ページ： Null  発行年： 2020年 
JST資料番号： W5058A  ISSN： 2589-1529  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 工学的焼結合金の改良された機械的性質を得るために,粉末特性の調整によるそれらの内部結晶粒界の最適化は,洗練された実践である。ここでは,新しいFe-Cu-(Ni+P)3重層複合粉末を得るために,粉末混合法における創造的要素ドーピングを堆積反応に基づいて報告した。その場γ-(Cu,Fe,Ni)界面相を有する多相微細構造を焼結したままのFe-Cu-Ni-P合金で開発し,より良い降伏強度(1538MPa)と塑性(23.3%)の組合せを達成した。本研究は,焼結材料における強度-塑性トレードオフジレンマを克服するための層状複合材料粉末の適用の成功裏の実証である。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  *塑性 ,  機械的性質 ,  結晶粒界 ,  *合金 ,  *最適化 ,  *焼結 ,  *粉体 ,  *焼結合金 ,  相乗作用 ,  ドーピング ,  焼結体 ,  降伏強さ
準シソーラス用語： *複合粉 , 【Automatic Indexing@JST】

著者キーワード (6件)： Fe-Cu-Ni-P合金 ,  層状複合粉末 ,  焼結プロセス ,  強度-塑性相乗作用 ,  微細構造のキャラクタリゼーション ,  機械的挙動

分類 (2件)： 圧粉,焼結  (WC02030X) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (11件)： 層状 ,  複合粉末 ,  ミクロ組織 ,  最適化 ,  Fe ,  Cu ,  Ni ,  焼結合金 ,  塑性 ,  衝突 ,  回避